1) Cu-Ni/SiO_2 bibasic catalyst
Cu-Ni/SiO2二元催化剂
1.
The Cu-Ni/SiO_2 bibasic catalyst was prepared by parallel flow precipitation method.
采用并流沉淀法制备了Cu-Ni/SiO2二元催化剂,研究了影响催化剂活性的主要因素:Cu/Ni比,SiO2加入量,焙烧温度和焙烧时间,得到最佳制备条件:Cu/Ni=1/2。
2) Cu-Ni/SiO_2 catalyst
Cu-Ni/SiO2催化剂
3) Cu/SiO2 catalyst
Cu/SiO2催化剂
1.
Cu/SiO2 catalysts were prepared by homogeneous deposition-precipitation of the mixture of aqueous cuprammonia complex and silica sol,accompanied by heating to remove ammonia.
采用均匀沉淀沉积法制备Cu/SiO2催化剂。
2.
The Cu/SiO2 catalyst for gas-phase hydrogenation of diethyl oxalate(DEO) to ethylene glycol(EG) was prepared by sol-gel method.
用溶胶-凝胶均匀沉淀法制备了草酸二乙酯气相加氢制乙二醇的Cu/SiO2催化剂。
4) Ni/SiO2 catalyst
Ni/SiO2催化剂
5) Ni-Cu catalyst
Ni-Cu催化剂
1.
Study on Ni-Cu catalysts for preparing o-phenylphenol;
制备邻苯基苯酚的Ni-Cu催化剂研究
6) Cu/SiO2? Cu/Zn/SiO2Catalyst
Cu/SiO2、Cu/Zn/SiO2催化剂
补充资料：Cu-A1-Ni shape memory alloy
分子式：
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。
CAS号：
性质：一种含A1 14％～14.5％(质量)、Ni 3％～4.5％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在133～373K之间。该合金的形状记忆应变约4％，它的热循环特性、形变循环特性和疲劳特性等均比TiNi形状记忆合金差。熔炼与Cu-Zn-A1形状记忆合金相同。该合金加工性很差，冷加工完全不可能。它的另一突出问题是随时间增长而记忆严重衰退的现象，为了提高合金的稳定性，可以进行等温淬火或一般淬火后进行时效处理。在Cu-A1-Ni形状记忆合金基础上开发出的Cu12Al5Ni2MnTi％(质量)五元高温形状记忆合金，铝含量降低，并加入Mn、Ti后，使Ms点提高到473K，同时合金的加工性亦得到改善，使Cu-A1-Ni系形状记忆合金成为具有实用价值的材料。