1) UHMWPE fiber
超高相对分子质量聚乙烯纤维
1.
The drawing parameters of UHMWPE fibers after gel spinning, initial drawing and extraction was decided by theoretical analysis on the drawing temperature and drawing ratio of UHMWPE fibers.
通过对冻胶纺丝、初步拉伸、再萃取后的超高相对分子质量聚乙烯纤维 (UHMWPE)的拉伸温度、拉伸倍数、热定型温度等的理论分析 ,指出 U HMWPE的拉伸温度应设定在熔点附近 ,确定了拉伸倍数及定型时应满足的拉伸倍数公式 ,热定型温度应低于上一道拉伸温度。
2.
Initial modulus of monofilament and multifilament were characterized for the test of UHMWPE fiber(SK75) and aramid fiber(Twaron2000) on a universal Instron Tensile Tester.
采用万能材料试验机对超高相对分子质量聚乙烯纤维(SK75型)和芳纶(Twaron2000型)两种样品的单丝、复丝模量进行了表征。
3.
Study on synthesize and application of neoprene adhesive for UHMWPE fiber;
应用结果表明改性氯丁橡胶粘合剂可用于超高相对分子质量聚乙烯纤维的上胶。
2) ultrahigh molecular weight polyethylene fiber
超高相对分子质量聚乙烯纤维
3) three-dimensionally braided PE-UHMW fiber
三维编织超高相对分子质量聚乙烯纤维
4) high molecular weight polyethylene fiber
高相对分子质量聚乙烯纤维
5) ultrahigh molecular weight polyethylene fiber
超高分子量聚乙烯纤维
1.
Improvement of ultrahigh molecular weight polyethylene fibers′ interface property by atmospheric argon plasma;
常压氩等离子体改善超高分子量聚乙烯纤维的界面性能
6) UHMWPE fibers
超高分子量聚乙烯纤维
1.
Continuous surface modification of UHMWPE fibers;
连续表面处理超高分子量聚乙烯纤维的研究
2.
Methods UHMWPE fibers and HDPE films were treated by H2O2 with hydrogen peroxidase.
方法以过氧化氢酶为催化剂,在H2O2存在下,氧化刻蚀超高分子量聚乙烯纤维(UHMWPE)和高密度聚乙烯膜(HDPE)。
补充资料：超高分子量聚乙烯醇纤维
分子式：
CAS号：
性质：所用原料聚乙烯醇的分子量特高的聚乙烯醇纤维。日本一公司用聚合度达23000、皂化度为99.9％(mol)的聚乙烯醇做原料，采用二甲基亚砜与乙二醇的混合液为溶剂，于145℃左右进行纺丝，压入低温(-2℃)的、由乙醇、二甲基亚砜和乙二醇组成的凝固浴中固化成形，成为透明的初生丝，再经特种后加工后(包括分多段进行超倍拉伸)即得成品。该纤维的强度可达28.8cN/dtex，模量达532.4cN/dtex；弯曲疲劳性、干热老化性和耐磨性均良好；产品适用于制作橡胶和建筑材料的补强材料。
CAS号：
性质：所用原料聚乙烯醇的分子量特高的聚乙烯醇纤维。日本一公司用聚合度达23000、皂化度为99.9％(mol)的聚乙烯醇做原料，采用二甲基亚砜与乙二醇的混合液为溶剂，于145℃左右进行纺丝，压入低温(-2℃)的、由乙醇、二甲基亚砜和乙二醇组成的凝固浴中固化成形，成为透明的初生丝，再经特种后加工后(包括分多段进行超倍拉伸)即得成品。该纤维的强度可达28.8cN/dtex，模量达532.4cN/dtex；弯曲疲劳性、干热老化性和耐磨性均良好；产品适用于制作橡胶和建筑材料的补强材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条