1) potassium tetratitanate film
四钛酸钾薄膜
1.
A new nanosmooth potassium tetratitanate film was prepared on glass substrates by a sol-gel method using Ti(n-OC_4H_9)_4 and CH_3COOK as precursors.
在四钛酸钾薄膜上进行十八烷基三氯硅烷(OTS)的自组装,通过测量自组装单分子膜(SAMs)因光催化分解而导致接触角变化研究薄膜的光催化性能。
2) potassium dititanate film
二钛酸钾薄膜
1.
Preparation and gaseous photocatalytic activity of smooth potassium dititanate film;
平整二钛酸钾薄膜的制备及其气相光催化活性
3) potassium hexatitanate film
六钛酸钾薄膜
4) potassium titanate biological thin film
钛酸钾生物薄膜
1.
Fabrication and biocompatibility in vitro of potassium titanate biological thin film/titanium alloy biological composite;
钛酸钾生物薄膜/钛合金生物复合材料的制备及其体外生物相容性
5) potassium tetratitanate
四钛酸钾
1.
The results indicate that potassium hexatitanate has better thermal stability than potassium tetratitanate.
结果表明:四钛酸钾(K2Ti4O9)的热稳定性低于六钛酸钾(K2Ti6O13)的。
2.
The test results indicate that meta-stable transformation of potassium tetratitanate begins at 950 ℃ or so,then finishes completely at higher than 1 100 ℃ and maintained for 2 h.
实验发现:在约950℃,四钛酸钾(K2Ti4O9)开始出现亚稳转变,1100℃以上保温2h后,其临界转变基本完成,说明K2Ti4O9是高温亚稳相,低于临界反应温度合成的六钛酸钾(K2Ti6O13)是由K2Ti4O9的亚稳相转变获得的。
6) SrTiO3 thin film
钛酸锶薄膜
1.
SrTiO3 thin film is made by sol-gol method with appropriate consistency.
首次对溶胶凝胶法中两种不同螯合剂柠檬酸和乙酰丙酮的螯和作用机理进行详细讨论,通过红外光谱、X射线衍射以及扫描电镜分析比较,采用乙酰丙酮为螯合剂制备得到的钛酸锶薄膜氧敏响应性高。
补充资料：四草酸根合铀(Ⅳ)酸钾
分子式：K4[U(C2O4)4]
CAS号：
性质：绿色晶体。将草酸铀U(C2O4)2溶于草酸钾溶液，浓缩得其结晶。有两对光学异构体。
CAS号：
性质：绿色晶体。将草酸铀U(C2O4)2溶于草酸钾溶液，浓缩得其结晶。有两对光学异构体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。