1) microwave pyrolysis CVI
微波热解CVI
1.
The textures of samples were observed,the densification rules of microwave pyrolysis CVI were analyzed by densification rate and radial-direction density distribution with different residence time.
2s)对微波热解CVI工艺制备炭/炭复合材料的致密化速率、样品的体积密度及其密度均匀性的影响,并对其组织结构进行了观察。
2) thermal gradient CVI
热梯度CVI
1.
Microstructure and properties of C/C composites prepared by thermal gradient CVI process;
热梯度CVI C/C材料的结构与性能
2.
Using nitrogen, hydrogen respectively as the carrier gas, the C/C composite was fabricated by the thermal gradient CVI process under the condition of 1000℃,0.
在1000℃,0 5kPa丙烯分压条件下,以N2、H2为载气和无载气情况下于热梯度CVI炉中制备了C/C复合材料,研究了载气特别是氢气对材料基体热解炭显微结构的影响。
3.
The carbon cloth and carbon fiber felt are laminated alternately and then needled to prepare the porous carbon/carbon preforms, from which the carbon/carbon composites for aircraft brakes are fabricated by the thermal gradient CVI process.
以炭布与炭纤维薄毡交替成叠层 ,采用针刺技术在垂直布面方向引入增强纤维 ,制成准三维预制体 ,在自行研制的热梯度CVI炉中制备了航空刹车用C/C复合材料 ;采用偏光显微镜研究了沉积炭的显微结构 。
4) Microwave heating sample digestion
微波加热试样消解
5) Microwave heated sample digestion
试样的微波加热消解
6) isobaric thermal gradient CVI
等压热梯度CVI
补充资料：废物热解
分子式：
CAS号：
性质：是在缺氧或无氧条件下废物的热分解过程。热解温度为500～800℃，比焚烧温度低。有机废物的热解可得到能分离、回收和再利用的气体或液体燃料。另外，由于热解温度相对较低，因此热解过程产生的氮氧化物(NOχ)少，而且尾气排放量也少。目前，发达国家已有城市垃圾、废塑料和废轮胎热解处理的工业化装置，但成功运行的这类工业化装置毕竟还很少，因此从总体来说，废物热解技术尚处在试验性生产的中试阶段。
CAS号：
性质：是在缺氧或无氧条件下废物的热分解过程。热解温度为500～800℃，比焚烧温度低。有机废物的热解可得到能分离、回收和再利用的气体或液体燃料。另外，由于热解温度相对较低，因此热解过程产生的氮氧化物(NOχ)少，而且尾气排放量也少。目前，发达国家已有城市垃圾、废塑料和废轮胎热解处理的工业化装置，但成功运行的这类工业化装置毕竟还很少，因此从总体来说，废物热解技术尚处在试验性生产的中试阶段。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条