1) fluorosilcone monomer
氟硅单体
1.
Acrylate copolymer latexes containing fluorosilicone units were prepared via core-shell emulsion copolymerization of methacrylate(MMA),butyl acrylate(BA) and fluorosilcone monomer which was prepared by fluorinated alcohol and vinyltriethoxyl silane.
以氟醇RfCH2CH2OH和乙烯基硅氧烷VTES为原料合成的氟硅单体,与甲基丙烯酸甲酯、丙烯酸丁酯在复合乳化体系中通过核壳乳液聚合制备了稳定的氟硅共聚乳液。
2.
In this paper, acrylate copolymer latexes containing fluorine and silicon were prepared via batch and core-shell emulsion copolymerization of methacrylate(MMA),butyl acrylate(BA) and fluorosilcone monomers.
以氟醇(RfCH2CH2OH)和乙烯基硅氧烷(A-151)为原料合成氟硅单体,然后在十二烷基硫酸钠(SDS)/辛基苯基聚氧乙烯醚(OP-10)复合乳化剂,过硫酸钾(KPS)引发剂存在下,分别采用间歇乳液聚合法和核壳乳液聚合法将其与甲基丙烯酸甲酯(MMA)、丙烯酸丁酯(BA)进行乳液共聚,制备含氟硅的丙烯酸酯共聚物乳液。
2) Organosilicon modification
共氟硅单体
3) fluorosilicone pre-polymer
氟硅预聚体
4) H_2SiF_6 solution
硅氟酸体系
1.
Review on indium solvent extraction with P_(204) from H_2SiF_6 solution
硅氟酸体系P_(204)萃取铟工艺评述
5) fluorine-containing monomers
含氟单体
1.
Three novel fluorine-containing monomers: 2-[(trifluoroacetyloxy)]ethyl methacrylate (TFAOEMA), 2-[(trifluroacetyl)oxy]ethyl acrylate (TFAOEA), and 2-[(trifluroacetyl)oxy]propyl acrylate (TFAOPA), were successfully synthesized.
以 (甲基 )丙烯酸羟烷基酯与三氟乙酐反应合成了三种新型含氟单体 :甲基丙烯酸三氟乙酰氧乙酯、丙烯酸三氟乙酰氧乙酯和丙烯酸三氟乙酰氧丙酯 。
6) fluorine monomer
氟单体
1.
This paper has mainly researched the prep(?)ation of fluoroacrylate as one kind of surface sizing agent by emulsion polymerization, using self- maded cationic polymeric emulsifier, and styrene、butyle acrylate、fluorine monomer as the material.
本文主要研究了采用自制阳离子高分子乳化剂,以苯乙烯、丙烯酸丁酯和含氟单体为原料进行乳液聚合,合成含氟丙烯酸酯表面施胶剂,确定最佳合成工艺条件,并进行放大生产,还对合成产品进行表征。
2.
The structure of the resin was attributed by infrared spectrum, and the acid proof, water resistant, the kali resistivity performance of it was tested, through which the relationship between fluorine monomer amount, functional monomer amount and the resin properties was discovered.
运用常规溶剂体系制备了含氟丙烯酸酯树脂,研究了含氟丙烯酸聚合物的影响因素,用红外光谱表征了树脂的结构,制膜后进行耐酸、耐水和耐碱性能的测定,找出了树脂性能与氟单体用量、功能单体用量之间的关系。
补充资料：有机硅单体
制备硅油、硅橡胶、硅树脂以及硅烷偶联剂的原料是各种有机硅单体，由几种基本单体可生产出成千种有机硅产品。有机硅单体主要有：甲基氯硅烷（简称甲基单体）、苯基氯硅烷（简称苯基单体）、甲基乙烯基氯硅烷、乙基三 氯硅烷、丙基三氯硅烷、乙烯基三氯硅烷、γ-氯丙基三氯硅烷和氟硅单体等。其中甲基氯硅烷最重要，其用量占整个单体总量的90%以上，其次是苯基氯硅烷。
任何高分子材料的发展，关键在于单体技术的发展。有机硅工业的特点是集中的单体生产和分散的产品加工。因此，单体生产在有机硅工业中占重要的地位，单体的生产水平直接反映有机硅工业的发展水平。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条