1) Pt-Ru/CMK-3 catalyst
Pt-Ru/CMK-3催化剂
1.
The Pt-Ru particles of the Pt-Ru/CMK-3 catalyst were found to be with high alloying extent,small average size and low relative crystallinity when the Pt-Ru/CMK-3 catalysts was prepared with the general chemical reduction method in the mixture solution of tetrahydrofuran(THF)and H2O.
提出了在四氢呋喃(THF)和H2O混合溶液中用一般的化学还原法在室温下制备高合金化Pt-Ru/CMK-3催化剂的新方法。
2) Pt/CMK-3 catalyst
Pt/CMK-3催化剂
3) Pt/CMK-5 catalyst
Pt/CMK-5催化剂
5) Pt-Ru/C catalyst
Pt-Ru/C催化剂
1.
The Pt-Ru particles of the Pt-Ru/C catalyst were found to be with high alloying extent, small average size and low relative crystallinity when the Pt-Ru/C catalyst was prepared with the general chemical reduction method in the mixture solution of tetrahydrofuran (THF) and H2O.
与在纯水中制得的Pt-Ru/C催化剂相比,其Pt-Ru粒子的合金化程度高、平均粒径较小且相对结晶度低,因此,该催化剂对甲醇氧化的电催化活性远高于在纯水中制得的Pt-Ru/C催化剂。
2.
The electrocatalytic activity of the Pt-Ru/C catalyst for the methanol oxidation is much higher than that of the commercial E-TEK Pt-Ru/C catalyst with the similar average size and relative crystalli.
在含四氢呋喃(THF)的水溶液中,室温下用NaBH4还原H2PtC l6和RuC l3制得Pt-Ru/C催化剂。
3.
In this paper, we have investigated the reverse micelles method of Pt-Ru/C catalysts prepared for PEMFC.
一般采用引入其它金属元素来解决Pt催化剂CO中毒问题,研究较多的为Pt-Ru/C催化剂。
6) Pt-Ru-Ir / C
Pt-Ru-Ir/C催化剂
1.
Two Pt-Ir/C catalysts with different ratio and a Pt-Ru-Ir / C ca talyst were prepared.
以H2PtCl66H2O和H2IrCl66H2O为前驱体,通过化学还原共沉积方法制备得到了不同Pt、Ir比例的Pt-Ir/C催化剂,同时在Pt-Ru/C催化剂中添加一定量的Ir,得到Pt-Ru-Ir/C催化剂。