1) styrene-acrylonitrile copolymer
苯乙烯-丙烯腈共聚物
1.
Synthesis and characterization of polyethylene-octene copolymer grafting styrene-acrylonitrile copolymer;
乙烯-辛烯共聚物接枝苯乙烯-丙烯腈共聚物的合成及其表征
2.
]In an existing plant with a continuous-flow stirred tank reactor for manufacturing styrene-acrylonitrile copolymers(SAN)and styrene-maleic anhydride copolymers(SMA),a unique bulk copolymerization process was successfully developed for producing styrene-acrylonitrile-maleic anhydride terpolymer(SAM).
借助现有工业装置及苯乙烯-丙烯腈共聚物(SAN)和苯乙烯-顺酐共聚物(SMA)的生产经验,建立并实施了国内独有的苯乙烯-丙烯腈-顺酐三元共聚工艺,生产出苯乙烯系树脂新品种———苯乙烯-丙烯腈-顺酐共聚物(SAM)。
3.
A kind of melting blends called AEMS with high impact strength,high resistance to weather aging and yellow discolo-ration was prepared by blending styrene-acrylonitrile copolymer(SAN) and ethylene-propylenediene monomer(EPDM)-g-methyl methacrylate acrylonitrile(MAN),EPDM-g-MAN synthesized by solution graft copolymerization in advance.
用乙烯-丙烯-二烯烃三元共聚物(EPDM)与甲基丙烯酸甲酯-丙烯腈(简称MAN)进行溶液接枝共聚合,生成MAN接枝EPDM(EPDM-g-MAN)共聚物,用其与苯乙烯-丙烯腈共聚物(SAN)共混制备耐老化性能优异的熔融共混物(简称AEMS);研究了EPDM含量与AEMS力学性能的关系。
2) SAN
苯乙烯-丙烯腈共聚物
1.
The blends of SAN and EVA were extracted by 30/70 mixture of cyclohexane and acetone.
用体积比为３０／７０的环己烷／丙酮混合溶剂进行了苯乙烯－丙烯腈共聚物（ＳＡＮ）／乙烯－醋酸乙烯酯共聚物（ＥＶＡ）共混物的选择性溶解分离试验。
2.
Styrene-acrylonitrile copolymer(SAN)/high glue powder/organosilicon blend was prepared by melt blending technology.
利用熔融共混法制备了苯乙烯-丙烯腈共聚物(SAN)/高胶粉/有机硅共混物,研究了高胶粉和有机硅用量对共混物力学性能和流动性能的影响。
3) styrene acrylonitrile copolymer
苯乙烯丙烯腈共聚物
4) acrylonitrile styrene copolymer(AS)
丙烯腈苯乙烯共聚物(AS)
5) SAN
(苯乙烯/丙烯腈)共聚物
1.
Silane coupling agent is adopted to improve the compatibility between glass fiber(GF) and SAN.
利用硅烷偶联剂改善玻璃纤维(GF)与(苯乙烯/丙烯腈)共聚物(SAN)之间的相容性,采用聚烯烃弹性体(POE)接枝马来酸酐(POE-g-MAH)对GF增强SAN体系进行增韧,制备了综合性能较好的GF增强SAN材料。
6) acrylonitrile-styrene copolymer
丙烯腈-苯乙烯共聚物
1.
The adsorption isotherms and dynamic equilibrium curve of acrylonitrile-styrene copolymer(AS) on TATB have been measured by using UV method.
用紫外光谱法测定了丙烯腈-苯乙烯共聚物(AS)在TATB(三氨基三硝基苯)炸药上的吸附动力学曲线和吸附等温线,考察了温度、溶剂种类、吸附剂TATB的比表面积及其浓度对吸附行为的影响。
2.
Adsorbed amount of polymer binder acrylonitrile-styrene copolymer(AS)on the surface of explosive 1,3,5-triamino-2,4,6- trinitrobenzen(TATB)for different process conditions was qualitatively and quantitatively studied through different experiments.
通过不同的实验方法对不同工艺条件下高分子粘合剂丙烯腈-苯乙烯共聚物(AS)在三氨基三硝基苯(TATB)炸药表面上的吸附量进行了定量和定性的研究。
补充资料：丙烯腈-氯化聚乙烯-苯乙烯共聚物
分子式：
CAS号：
性质：ACS 系氯化聚乙烯与丙烯腈和苯乙烯接枝共聚物。它与ABS相比，具有良好耐候性和阻燃性。成型收缩率小，耐酸耐碱。拉伸强度31～39MPa，拉伸模量2000MPa，悬臂梁缺口冲击强度118～490J/m，热变形温度78～86℃，阻燃性UL94—HB或VO级。常用过氧化物引发剂进行悬浮聚合制得。主要用于有耐候和阻燃要求的电器、家电制品、车辆、建材、机械配件及家具、照明器材、包装等。
CAS号：
性质：ACS 系氯化聚乙烯与丙烯腈和苯乙烯接枝共聚物。它与ABS相比，具有良好耐候性和阻燃性。成型收缩率小，耐酸耐碱。拉伸强度31～39MPa，拉伸模量2000MPa，悬臂梁缺口冲击强度118～490J/m，热变形温度78～86℃，阻燃性UL94—HB或VO级。常用过氧化物引发剂进行悬浮聚合制得。主要用于有耐候和阻燃要求的电器、家电制品、车辆、建材、机械配件及家具、照明器材、包装等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条