1) curing agent
硫化剂
1.
Application of curing agent DL 268 to NR/SBR compound;
硫化剂DL-268在NR/SBR胶料中的应用
2.
The application and progress of trimerization thiocyanic acid as curing agent of acrylate rubber,polychloroether elastomer,tackifier for curing adhesion of rubber and metal,and as crosslinking agent of other rubber and plastic products were introduced in details.
本文详细介绍了三聚硫氰酸作为丙烯酸酯橡胶和聚氯醚弹性体硫化剂、橡胶与金属直接硫化粘合增粘剂以及其它橡塑产品交联剂的应用现状和最新进展,并提出了三聚硫氰酸的发展趋势。
3.
5 ENR with 1~2 phr curing agent DCP and secondary curing a.
采用硫黄硫化体系和过氧化物(硫化剂DCP)硫化体系对EPDM/NR并用胶实施复合交联,研究并用比和复合交联体系对胶料的硫化特性、物理性能和耐热老化性能的影响。
2) vulcanizing agent
硫化剂
1.
High performance sealing rubber used for ships (Ⅰ) The effect of vulcanizing agent on the physical properties of fluorinated rubber vulcanizate;
舰船用高性能密封橡胶研究 (Ⅰ)硫化剂对氟橡胶硫化胶物理性能的影响
2.
Effects of vulcanizing agents on the performance of the CPE-bonded magnet;
硫化剂对CPE粘结磁体性能的影响
3) vulcanizator
硫化剂
1.
The best conditions are the reaction temperature of 45 ℃, pH 4 and the ratio of 1 to 20(w%) of vulcanizator to galena, accordingly, the contents of Fe and Pb in the solution are under 1 mg/L.
结果表明,pH=4时,采用针铁矿法除铁,能有效去除浸出液中的Fe离子;在温度为45℃、pH=4、硫化剂与方铅矿的质量比为1∶20时,采用硫化法去除重金属,浸出液中的Fe、Pb杂质含量均小于1mg/L,满足制备工艺要求。
2.
－ bis(natriumthiosulfate) hexane was prepared using 1,6－ dichlorohexane and sodium thiosulfate, after that a new vulcanizator 1,6－ bis(diethylthiocarbamoyl－ disulfide)hexane was prepared and characterized by IR and MS.
用 1， 6－二氯己烷与硫代硫酸钠合成了六亚甲基－ 1,6－二硫代硫酸二钠盐，进而制备了新型硫化剂双－ 1,6－ (二乙基硫代氨甲酰－二硫化 )己烷。
4) curative
[英]['kjʊərətɪv] [美]['kjurətɪv]
硫化剂
1.
Application of curative DTDM to ply compound of bias truck tire;
硫化剂DTDM在斜交轮胎内外层胶料配方中的应用
2.
The effects of the accelerator NA-22 curing system and triazine-mercaptan(including curatives AF and TCY) curing system on the properties of epichlorohydrin binary copolymer(CHC) were investigated.
探讨促进剂NA 22硫化体系和三嗪硫醇(包括硫化剂AF和TCY)硫化体系对二元共聚氯醚橡胶(CHC)性能的影响。
5) sulfiding agent
硫化剂
1.
The results showed that the exothermal temperature was higher when certain single sulfide was added to catalyst as sulfiding agent and the same result was obtained with two kinds of sulfides combined simply.
结果发现,单一硫化物或不同硫化物作为硫化剂简单添加时,器外预硫化催化剂上放热明显;而经过对硫化剂添加方式或制备方案的改进,则可以大幅度地降低催化剂上的局部集中放热。
6) sulfurless vulcanizing agent
无硫硫化剂
补充资料：硫化剂
分子式：
CAS号：
性质：又称交联剂。能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加的物质。除了某些热塑性橡胶不需要硫化外，天然橡胶和各种合成橡胶都需配入硫化剂进行硫化。橡胶经硫化后才具有宝贵的使用价值，力学性能大大提高。橡胶硫化剂包括元素硫、硒、碲，含硫化合物，过氧化物，醌类化合物，胺类化合物，树脂类化合物，金属氧化物以及异氰酸酯等。用得最普遍的是元素硫和含硫化合物。硫化剂适用于各类天然橡胶和合成橡胶，根据需要，不同的硫化剂品种可配合使用。
CAS号：
性质：又称交联剂。能使橡胶分子链起交联反应，使线形分子形成立体网状结构，可塑性降低，弹性剂强度增加的物质。除了某些热塑性橡胶不需要硫化外，天然橡胶和各种合成橡胶都需配入硫化剂进行硫化。橡胶经硫化后才具有宝贵的使用价值，力学性能大大提高。橡胶硫化剂包括元素硫、硒、碲，含硫化合物，过氧化物，醌类化合物，胺类化合物，树脂类化合物，金属氧化物以及异氰酸酯等。用得最普遍的是元素硫和含硫化合物。硫化剂适用于各类天然橡胶和合成橡胶，根据需要，不同的硫化剂品种可配合使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。