1) carbonized aerogel powder
碳气凝胶粉末
2) Aerogel powder
气凝胶粉末
1.
Organic and carbon aerogel powder was prepared by sol-gel method with the help of ultrasonic emulsification technology using resocinol and formaldehyde.
利用超声波乳化技术结合溶胶-凝胶反应制备了间苯二酚-甲醛有机气凝胶粉末和碳化气凝胶粉末,并对所制备的有机气凝胶和碳气凝胶粉末进行了表征和讨论。
3) organic aerogel powder
有机气凝胶粉末
1.
Upon pyrolysis of organic aerogel powder at high temperature,the carbonized aerogel can be obtained.
间苯二酚-甲醛有机气凝胶粉末经过高温碳化处理得到其碳气凝胶粉末。
4) carbon aerogel
碳气凝胶
1.
The microstructure of carbon aerogel was investigated by using electron scanning microscope(SEM),pore size distribution and electrical conductivity measurement.
探索新型纳米多孔材料碳气凝胶的微结构控制,研究常压条件下纤维增强型碳气凝胶的制备,以及催化剂浓度、质量分数、纤维表面特性、溶胶注入纤维前的老化时间等制备参数对其微结构的影响。
2.
This paper examins carbon aerogel by SEM, BET and cyclic voltammetry.
在常压条件下通过溶胶-凝胶法和碳化、活化工艺制备碳气凝胶材料。
3.
The micro structure of the porous carbon aerogels is measured by SEM and BET.
经高温碳化处理 ,将RF有机气凝胶转化为碳气凝胶 ,改变RC比和聚合单体的质量百分数 ,可控制气凝胶的粒径及孔径、密度及比表面积。
5) carbon aerogels
碳气凝胶
1.
For the first time,hydroquinone-formaldehyde aerogels have been prepared by sol-gel method and CO_2 supercritical drying,and after high temperature carbonization the carbonized carbon aerogels are obtained.
首次用溶胶-凝胶法和CO2超临界干燥技术制备了对苯二酚-甲醛有机气凝胶,并经高温碳化处理得到其碳气凝胶,测得气凝胶的比表面积由碳化前的375。
2.
In this paper, carbon aerogels are obtained through ordinary pressure drying; their structural properties are investigated.
碳气凝胶是一种新型多孔碳材料,具有比表面积大、电导率高的特点。
3.
SEM, BET and pore size distribution techniques were used to characterize the morphology and pore structure of the carbon aerogels.
研究了碳气凝胶在常压条件下的制备过程和干燥方法。
6) Carbonized RF aerogels(CRF aerogels)
碳化气凝胶
1.
Carbonized RF aerogels(CRF aerogels) have large specific area, good conductivityand excellent electro-chemical stability.
其政化产物碳化气凝胶（CRF气凝胶）具有大的比表面积、好的导电性和电化学稳定性，成为制备超级电化学双层电容器也（SEDLCs）的理想电极材料。
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条