1) primary crystallization
初晶化
1.
Influence of rare earth and Ni content on the primary crystallization of Al-Gd-Er-Ni metallic glass;
稀土和镍含量对Al-Gd-Er-Ni金属玻璃初晶化的影响
2.
The influence of Be replacement for Al on the glass forming ability(GFA)and primary crystallization of Al85Gd7Ni8alloy was investigated.
研究了Be部分替代Al对Al85Gd7Ni8合金的玻璃形成能力和初晶化的影响。
2) energetic parameter
初晶化合物
1.
In this paper, the relationship between the energetic parameter f(r) of molten salt system and the ratio of primary crystallization compound has been exa mined.
在测定了ＬｉＣｌＭ′Ｃｌ２ＭＦ系列熔盐相图的基础上，讨论了ＬｉＣｌＭ′Ｃｌ２ＭＦ熔盐体系的初晶化合物摩尔比和溶解能参数的关系，并总结了多元相图中一些初晶化合物的形成规律。
3) Refinement of Primary Si Phase
初晶硅细化
5) initial frost crystal
初始霜晶
1.
The formation mechanisms of different initial frost crystal shapes were explained from a crystal growth point of view.
从晶体生长角度解释了各种形状初始霜晶的形成机制;利用界面稳定性理论分析指出:温度场和水蒸气浓度场是影响霜晶生长的主要因素,两者的竞争耦合作用是产生相变和霜晶各种界面演变现象的根本原因;建立了霜晶生长速率与霜晶表面温度及水蒸气分压力相关的数学模型。
6) liquidus temperature
初晶温度
1.
Effect of NaCl and LiF on liquidus temperature of molten cryolite-based aluminum electrolyte;
NaCl和LiF的添加对铝电解质初晶温度影响的研究
2.
Study on new device for testing liquidus temperature of aluminium electrolyte and mathematical model of liquidus temperature;
铝电解质初晶温度测定装置及初晶点数模的研究
3.
Study on direct determination of liquidus temperature of aluminium electrolyte;
直接测定铝电解质初晶温度的研究
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。