1) EVOH
乙烯-乙烯醇共聚物
1.
Preparation and Properties of TPS/EVOH Composites;
热塑性淀粉/乙烯-乙烯醇共聚物复合材料的制备与性能
2.
The melting,physical mechanical and the rheological properties of ethylene-ethenol(EVOH) were studied.
研究了乙烯-乙烯醇共聚物(EVOH)的热熔融性能、物理机械性能以及加工流变性能。
3.
Poly (ethylene-co-vinyl alcohol)(EVOH)hydroxyls comb polymer was prepared from alcohol and alkylogen.
以乙烯-乙烯醇共聚物(EVOH)为原料,制备了一种主链为疏水的聚乙烯链段,侧链具有亚乙氧基结构的多羟基梳形聚合物,用元素分析法、凝胶渗透色谱法、核磁共振谱法对其进行了结构表征;用热重分析法和示差扫描量热法对其热学性能进行了表征。
3) Poly(ethylene-co-vinyl alcohol)
乙烯-乙烯醇共聚物
1.
Poly(ethylene-co-vinyl alcohol)(EVOH)-based comb polymer was synthesized from poly(ethylene-co-vinyl alcohol)(EVOH) and ethylene oxide(EO) with the catalyst of sodium ethylate.
以乙烯-乙烯醇共聚物(EVOH)为原料,在乙醇钠的催化作用下,通过与环氧乙烷(EO)的反应,合成出侧链为醚链结构且端基为羟基的梳型聚合物。
4) EVAL
乙烯-乙烯醇共聚物
1.
Using ethylene vinyl alcohol copolymer(EVAL) as membrane matrix material,anion exchange resin D301R as functional particles,resin filled EVAL hollow fiber membrane are prepared by dry-wet spinning process.
以乙烯-乙烯醇共聚物(EVAL)为基质材料,阴离子交换树脂D301R为功能性颗粒,采用干-湿法制备了树脂填充EVAL中空纤维膜,并考察了凝固浴温度、聚合物质量分数对纯水通量、牛血清白蛋白(BSA)截留率的影响。
5) polyvinyl alcohol copolymer
聚乙烯醇共聚物
6) ethylene/vinyl alcohol copolymer
(乙烯/乙烯醇)共聚物
补充资料：乙烯-乙烯醇共聚物
分子式：
CAS号：
性质：化学结构上是乙烯与乙烯醇共聚物，实际上是乙烯-醋酸乙烯无规共聚物经水解而成的含羟基的半结晶性热塑性树脂。乙烯含量控制在25％～45％，具有极好的不透气和保芳香阻隔性，透明性和光泽好，耐油脂和化学药品，耐紫外线及其他射线，机械性能、强度和拉伸模量好。乙烯含量32％的产品，密度1.19g/cm3，熔体指数1.3g/10min，熔点181℃，拉伸强度19MPa，伸长率8％，透氧率40～60cm3μm/(m2·24h·105Pa)(23℃，0％RH)，透水蒸气速率1300～3400g·μm/(m2·24h)(38℃，90％RH)。阻隔性比尼龙大100倍，比聚乙烯、聚丙烯高10 000倍。但在高湿度时阻隔性下降。工业上采用乙烯-醋酸乙烯共聚物(EVA)水解而成。用作肉类、油脂、工业溶剂、农药等复合包装膜，发泡材料、中空容器的阻隔层。
CAS号：
性质：化学结构上是乙烯与乙烯醇共聚物，实际上是乙烯-醋酸乙烯无规共聚物经水解而成的含羟基的半结晶性热塑性树脂。乙烯含量控制在25％～45％，具有极好的不透气和保芳香阻隔性，透明性和光泽好，耐油脂和化学药品，耐紫外线及其他射线，机械性能、强度和拉伸模量好。乙烯含量32％的产品，密度1.19g/cm3，熔体指数1.3g/10min，熔点181℃，拉伸强度19MPa，伸长率8％，透氧率40～60cm3μm/(m2·24h·105Pa)(23℃，0％RH)，透水蒸气速率1300～3400g·μm/(m2·24h)(38℃，90％RH)。阻隔性比尼龙大100倍，比聚乙烯、聚丙烯高10 000倍。但在高湿度时阻隔性下降。工业上采用乙烯-醋酸乙烯共聚物(EVA)水解而成。用作肉类、油脂、工业溶剂、农药等复合包装膜，发泡材料、中空容器的阻隔层。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。