1) Ultrasonic Arc Spray Gas Atomization
超音速电弧喷射气雾化
1.
The fine powder of Ag-10Ni immiscible alloy was prepared by Ultrasonic Arc Spray Gas Atomization process.
采用超音速电弧喷射气雾化制粉设备制备了难固溶Ag-10Ni合金粉末。
2) Ultrasonic Arc Spray Atomization
超音速电弧喷射雾化
1.
Rapid Solidification of Cu-10Ag Alloy Droplets by Ultrasonic Arc Spray Atomization;
超音速电弧喷射雾化Cu-10Ag合金熔滴的快速凝固
2.
Ag-10Ni and Ag-5Fe alloy powders were prepared by ultrasonic arc spray atomization process.
采用超音速电弧喷射雾化制备Ag-10Ni、Ag-5Fe合金粉末,采用SEM对合金粉末的快速凝固组织特征进行研究。
3) Supersonic arc spraying
超音速电弧喷涂
1.
Analysis and simulation of nitrogen and oxygen content in coating prepared by titanium-aluminum twin wires supersonic arc spraying;
钛铝双丝超音速电弧喷涂层氮氧含量的分析与仿真
2.
This article briefs the present status and technical characteristies of various kinds of hot spraying techniques,and details the application status of supersonic arc spraying (SAS) technique in the life extension and restoration of power plant equipment,such as on the steel structural components,"four tubes" exposed surface,fan wheel,blades of steam turbines.
介绍了各种热喷涂技术的现状及其技术特性,并详细介绍了超音速电弧喷涂技术在电厂设备延寿修复中的应用情况,如在钢结构部件、“四管”爆漏、风机叶轮上、汽机叶片上的应用等。
3.
In this paper, based on the uniform design principle, an abrasive wear test of Ti-Al coating produced by supersonic arc spraying was conducted, and a stepwise regression analysis was made.
基于均匀设计试验设计方法,进行了超音速电弧喷涂Ti-Al 涂层磨粒磨损试验,在对试验结果进行逐次回归分析的基础上,系统并定量的研究了涂层耐磨性能随着喷涂工艺参数的变化规律,得到了优化后的最佳喷涂工艺参数。
4) supersonic arc spray
超音速电弧喷涂
1.
Electrochemical measurement of corrosion resistance and microstructure analyse of supersonic arc spray coating;
超音速电弧喷涂涂层耐蚀性的电化学测试及组织分析
2.
Al,Zn,316 stainless steel and ERNiCu-7 four kinds of coatings on the surface of steel plate were respectively sprayed by supersonic arc spray.
利用超音速电弧喷涂设备在钢板表面分别喷涂Al、Zn、316不锈钢(0CrNi12Mo2)和ERNiCu-7四种涂层,采用CHI660B电化学工作站测试四种材料在60%H2SO4溶液中的稳态极化曲线和Tafel斜率,并利用金相显微镜和X射线衍射等方法进行腐蚀前后的组织分析。
5) ultrasonic arc spraying
超音速电弧喷涂
1.
By means of homemade ultrasonic arc spraying system, Ti-Al alloy composites coatings were made on 45 steel surfaces.
结果表明 ,利用超音速电弧喷涂设备 ,可以在 4 5钢表面形成致密度高、孔隙率低 ,结合强度较好和硬度高的Ti Al合金涂层。
6) transonic electric arc spraying
超音速电弧喷涂
1.
Under the circumstance of the Circulating Fluidized Bed(CFB) boiler heating surface worn away seriously、repair frequently and high costs for operation and starting energy,adopting transonic electric arc spraying method to prevent the heating surface been abrasived.
针对循环流化床(CFB)锅炉受热面易严重磨损、检修频繁、启动能耗和运行成本高的情况,采用超音速电弧喷涂的方法,对受热面进行防磨处理,并对喷涂前后的使用状况进行了对比,分析了存在的问题。
2.
Under the circumstance of the Circulating Fluidized Bed boiler heating surface worn away seriously,adopting transonic electric arc spraying method to prevent the heating surface been abrasived.
针对循环流化床锅炉受热面磨损严重的情况,采用超音速电弧喷涂的方法,对受热面进行防磨处理,介绍了喷涂的工艺,喷涂后的材料表面状况,并对喷涂前后的使用状况进行了对比,对存在的问题进行了分析。
补充资料：超音速气体雾化快凝A1-Li合金粉末及其板材和棒材
超音速气体雾化快凝A1-Li合金粉末及其板材和棒材
超音：《气体霉化快凝A1．L1合金衍柬及}扳材和摔材
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条