1) chemical blackening
化学发黑
1.
The optimization of the process for the surface chemical blackening of 1Cr18Ni9Ti stainless steel was investigated using orthogonal test,aiming at improving the appearance quality and corrosion resistance of the blackening film.
为了提高1Cr18Ni9Ti不锈钢表面化学发黑膜的外观质量及耐蚀性能,通过正交试验研究了表面化学发黑优化工艺。
2.
A chemical blackening of aluminium alloys is proposed.
提出了铝合金化学发黑工艺,通过前处理、化学镀镍、电镀铜、再化学着黑色,可以获得高附着力、致密均匀的黑色氧化膜。
2) electrochemical blackening
电化学发黑
1.
Studies on the electrochemical blackening of alloy structural steel at room temperature;
合金结构钢常温电化学发黑工艺研究
2.
The potential appropriate for electrochemical blackening of copper was determined by examining cyclic voltammetric (CV) properties of copper in 0.
对铜在无硒电化学发黑液中的行为进行了研究。
3) oxidative blackening
氧化发黑
1.
A process for plating Sn on metal fasteners was introduced, including degreasing, halide Sn plating, oxidative blackening, polishing and varnishing.
介绍了一种金属钮扣电镀古锡的工艺,其主要工序包括除油、卤化物镀锡、氧化发黑、抛光、罩清漆等。
4) phosphatingblacking
磷化发黑
5) iron-normal-temperature-phosphating
发黑磷化
6) sulfide staining
硫化发黑
补充资料：发黑
分子式：
CAS号：
性质：又称发黑。钢铁表面处理的一种方法。通常将工件浸入强氧化性的化学溶液中。例如沸腾温度为147～152℃的氧氧化钠(600g/cm3)及亚硝酸钠(100g/cm3)水溶液中，经一定时间使表面生成一层美观、较致密且具有防锈作用的黑色氧化铁薄膜。此项工艺有时也混称“发蓝”。广泛应用于钟表、指针、游丝、螺钉、仪表外壳及某些机械的零件等。
CAS号：
性质：又称发黑。钢铁表面处理的一种方法。通常将工件浸入强氧化性的化学溶液中。例如沸腾温度为147～152℃的氧氧化钠(600g/cm3)及亚硝酸钠(100g/cm3)水溶液中，经一定时间使表面生成一层美观、较致密且具有防锈作用的黑色氧化铁薄膜。此项工艺有时也混称“发蓝”。广泛应用于钟表、指针、游丝、螺钉、仪表外壳及某些机械的零件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条