H抽出,H-test,在线英语词典,英文翻译,专业英语

1) H-test

H抽出

2) H pull-out method

H抽出

The methods of studying the interfacial bonding behavior between aramid cord and rubber was intraduced, and the static bonding behavior in the aramid cord/rubber composite was actually studied and evaluated using H pull-out method.

介绍了芳纶帘线-橡胶界面粘合性能的研究方法,并对芳纶帘线-橡胶复合材料静态粘合性能进行研究,采用H抽出对其进行评价。

3) H pull-out

H抽出力

The results showed that the t_(10)and t_(90)of rubber compound extended a little by using superfine active kaolin partly instead of carbon black in inner ply and outer ply compounds,and the physical properties of vulcanizate and H pull-out after aging changed little;the endu-rance of finished tire improved and the cost of rubber compound reduced.

结果表明,在内层和外层帘布胶中以超细活性高岭土部分替代炭黑后,胶料的t10和t90稍有延长,硫化胶的物理性能及老化后H抽出力基本相当;成品轮胎耐久性能提高,胶料成本降低。

The results showed that the scorch time extended,the curing speed reduced,the anti-reversion improved,and the better tensile,elongation and tear properties were obtained using TBSI instead of TBBS by equal weight in the upper bead filler compound;and the scorch time extended,t_(90) reduced,the permanent tensile set decreased and the H pull-out changed little using 1 phr of TBSI instead of 1.

在胎体胶配方中以 1份促进剂TBSI替代 1 2 5份促进剂DZ ,胶料的焦烧时间延长 ,t90 缩短 ,硫化胶的拉断永久变形减小 ,H抽出力相当。

4) H pull-out force

H抽出力

The results showed that when compared to the dry cobalt decanoate,the wet cobalt decanoate gave NR vulcanizate higher H pull-out force,lower H pull-out force loss after hot air aging and brine aging and similar physical properties.

结果表明,与干法工艺生产的癸酸钴相比,采用湿法工艺生产的癸酸钴可提高NR硫化胶的H抽出力,经热空气老化和盐水老化后硫化胶的H抽出力下降率较小,其它物理性能基本相当。

5) adhesion by H test

H抽出值

Experiments on changing fomula of nylon6 dip solution find that there has a constant ratio betwen RFL viscosity and adhesion by H test of nylon6 dipped cord fabric.

通过对浸胶液处方的调整试验 ,发现RFL液粘度与帘子布H抽出值之间存在比例关系 ,从而可以用RFL液粘度推算帘子布的H抽出值大

6) H-test

“H”抽出

补充资料：H抽出

分子式：
CAS号：

性质：测定帘子线与橡胶间附着力的指标。黏着力大，帘子线(布)与橡胶的黏着性能良好。试验方法为将帘子线试样嵌入按配方制成的橡胶片内，在规定的压力、温度和时间内硫化，修整成规定规格的“H”型试片，用强力机中测定从试片中抽出帘子线的力。

说明：补充资料仅用于学习参考，请勿用于其它任何用途。

首页 \| 翻译 \| 影视 \| 论坛 \| 索引

1) H-test H抽出 2) H pull-out method H抽出 1. The methods of studying the interfacial bonding behavior between aramid cord and rubber was intraduced, and the static bonding behavior in the aramid cord/rubber composite was actually studied and evaluated using H pull-out method. 介绍了芳纶帘线-橡胶界面粘合性能的研究方法,并对芳纶帘线-橡胶复合材料静态粘合性能进行研究,采用H抽出对其进行评价。 3) H pull-out H抽出力 1. The results showed that the t_(10)and t_(90)of rubber compound extended a little by using superfine active kaolin partly instead of carbon black in inner ply and outer ply compounds,and the physical properties of vulcanizate and H pull-out after aging changed little;the endu-rance of finished tire improved and the cost of rubber compound reduced. 结果表明,在内层和外层帘布胶中以超细活性高岭土部分替代炭黑后,胶料的t10和t90稍有延长,硫化胶的物理性能及老化后H抽出力基本相当;成品轮胎耐久性能提高,胶料成本降低。 2. The results showed that the scorch time extended,the curing speed reduced,the anti-reversion improved,and the better tensile,elongation and tear properties were obtained using TBSI instead of TBBS by equal weight in the upper bead filler compound;and the scorch time extended,t_(90) reduced,the permanent tensile set decreased and the H pull-out changed little using 1 phr of TBSI instead of 1. 在胎体胶配方中以 1份促进剂TBSI替代 1 2 5份促进剂DZ ,胶料的焦烧时间延长 ,t90 缩短 ,硫化胶的拉断永久变形减小 ,H抽出力相当。 4) H pull-out force H抽出力 1. The results showed that when compared to the dry cobalt decanoate,the wet cobalt decanoate gave NR vulcanizate higher H pull-out force,lower H pull-out force loss after hot air aging and brine aging and similar physical properties. 结果表明,与干法工艺生产的癸酸钴相比,采用湿法工艺生产的癸酸钴可提高NR硫化胶的H抽出力,经热空气老化和盐水老化后硫化胶的H抽出力下降率较小,其它物理性能基本相当。 5) adhesion by H test H抽出值 1. Experiments on changing fomula of nylon6 dip solution find that there has a constant ratio betwen RFL viscosity and adhesion by H test of nylon6 dipped cord fabric. 通过对浸胶液处方的调整试验 ,发现RFL液粘度与帘子布H抽出值之间存在比例关系 ,从而可以用RFL液粘度推算帘子布的H抽出值大 6) H-test “H”抽出补充资料：H抽出分子式： CAS号：性质：测定帘子线与橡胶间附着力的指标。黏着力大，帘子线(布)与橡胶的黏着性能良好。试验方法为将帘子线试样嵌入按配方制成的橡胶片内，在规定的压力、温度和时间内硫化，修整成规定规格的“H”型试片，用强力机中测定从试片中抽出帘子线的力。说明：补充资料仅用于学习参考，请勿用于其它任何用途。