1) Zr-Sn-Nb zirconium-based alloy
Zr-Sn-Nb锆合金
2) Zr-Sn-Nb new zirconium alloys
Zr-Sn-Nb新锆合金
1.
The specimens of Zr-Sn-Nb new zirconium alloys were treated in different ways at 1 045 ℃/40 min+500 ℃/1.
5 h工艺,将Zr-Sn-Nb新锆合金加工成厚度为1。
3) Zr-Sn-Nb-Fe-Cr zirconium alloy
Zr-Sn-Nb-Fe-Cr锆合金
1.
The mechanical properties and corrosion resistance of the sample made by vacuum electron bean welding of Zr-Sn-Nb-Fe-Cr zirconium alloy were investigated.
研究了Zr-Sn-Nb-Fe-Cr锆合金真空电子束焊接样品的拉伸和抗腐蚀性能,结果表明,焊接样品室温和375℃的拉伸性能略低于母材;焊接样品在500℃过热蒸汽中腐蚀500 h未出现疖状腐蚀现象,但腐蚀增重略大于母材;在400℃过热蒸汽中腐蚀320 d及360℃水中腐蚀520d,样品焊缝处颜色均为黑亮,未出现白色、棕色等腐蚀产物。
4) Zr-Sn-Nb alloy
Zr-Sn-Nb合金
1.
The specimens of Zr-Sn-Nb alloy with two different composition were treated in different ways as 1 000 ℃-0.
将两种Zr-Sn-Nb合金样品分别进行1000℃-0。
2.
Hot-rolling, cold-rolling and quenching tests of Zr-Sn-Nb alloy were carried out at 750℃, 780℃, 800℃ and 820℃, respectively.
对Zr-Sn-Nb合金在4种温度(750℃、780℃、800℃和820℃)下进行了热/冷加工和最终再结晶退火,并对在上述4种温度下加热的试样进行了淬火处理。
3.
The corrosion products on the I-SCC fracture of Zr-Sn-Nb alloys have been investigated by SEM and EDXA.
利用SEM和EDXA对Zr-Sn-Nb合金碘致应力腐蚀断口上的腐蚀产物进行了观察分析。
5) Zr-Sn-Nb-Fe-Cr alloy
Zr-Sn-Nb-Fe-Cr合金
1.
The hot deformation behaviors of Zr-Sn-Nb-Fe-Cr alloy in the thermal range of 600-980 ℃ and strain rate range of 0.
应用Gleeble-1500热模拟机对Zr-Sn-Nb-Fe-Cr合金进行热压缩试验,研究该合金在600~980℃和应变速率0。
6) TLM(Ti-3Zr-2Sn-3Mo-15Nb) alloy
TLM(Ti-Zr-Sn-Mo-Nb)合金
补充资料：锆合金
| 锆合金 zirconium alloy 以锆为基体加入其他元素而构成的有色合金。主要合金元素有锡、铌、铁等。锆合金在300～400℃的高温高压水和蒸汽中有良好的耐蚀性能、适中的力学性能、较低的原子热中子吸收截面，对核燃料有良好的相容性，多用作水冷核反应堆的堆芯结构材料。此外，锆对多种酸、碱和盐有优良的抗蚀性，与氧、氮等气体有强烈的亲和力，因此锆合金也用于制造耐蚀部件和制药机械部件，在电真空和灯泡工业中被广泛用作非蒸散型消气剂。 工业规模生产的锆合金有锆锡系和锆铌系两类。前者合金牌号有Zr-2、Zr-4，后者的典型代表是Zr-2.5Nb。在锆锡系合金中，合金元素锡、铁、铬、镍可提高材料的强度 、耐蚀性和耐蚀膜的导热性，降低表面状态对腐蚀的敏感性 。通常Zr-2合金用于沸水堆 ，Zr-4 合金用于压水堆 。在锆铌系合金中，铌的添加量达到使用温度下锆的晶体结构的固溶极限时，合金的耐蚀性最好。锆合金有同质异晶转变，高温下的晶体结构为体心立方，低温下为密排六方。锆合金塑性好，可通过塑性加工制成管材、板材、棒材和丝材；其焊接性也好，可用以进行焊接加工。 |