2) equivalent curing
等效硫化
1.
The model was applied in the adaptive control of the equivalent curing of thick rubber products.
00-35 42PR工程机械轮胎进行硫化测温的基础上,基于人工神经网络对厚橡胶制品内部温度建模,并应用模型参考自适应控制方案对厚橡胶制品进行等效硫化控制。
2.
And analyzed the equivalent curing of tire using steam and nitrogen gas duringthe cycle and put forward the relative curing condition.
对轮胎蒸汽/氮气硫化过程的等效硫化问题进行了分析研究,提出了相应的硫化条件。
3) equivalent curing value
等效硫化值
4) equivalent vulcanization time
等效硫化时间
1.
With the properties of Equivalent Vulcanization temperature,three alarming outputs of the Temperature Controller are used to determine temperature interzone of Vulcanization tank,and Equivalent Vulcanization Time is adjusted.
应用范特霍夫理论,研究了等效硫化下温度与时间的区间特性,根据等效硫化温度的区间特性,利用温控表的三个报警输出来确定硫化罐所处温度区间,调整等效硫化时间,并与上位机进行实时通讯。
5) rubber equivalent stilphtirising
橡胶等效硫化
6) curing effect
硫化效应
1.
During the transfer from pot curing to continuous curing, many manufacturers made production by modifying rubber compound formulation, This article demonstrates theoretically that instead of modifying rubber compound formulation it is possible to realize condition transformation by using the principle of equal curing effect, thus saving the tedious work of modifying formulation.
很多厂家从罐硫向连硫过渡的过程中 ,都是采用修改橡皮配方的办法 ,而本文从理论上详细介绍了不需改变橡皮配方而通过硫化效应相等原则直接进行条件变换即可 ,从而避免了研究橡皮配方的烦恼 ,并由我厂实际情况验证是可行
补充资料：等效硫化
分子式：
CAS号：
性质：橡胶制品硫化程度的深浅可用硫化效应来表示，硫化效应相等即等效硫化。即E=Iτ。式中，E为硫化效应；I为硫化强度；τ为硫化时间。硫化强度是胶料在某温度下，单位时间内达到的硫化程度，即I=K(t-t0)/10；式中，K为硫化温度系数(一般取K=2)；t为硫化温度；t0规定硫化效应用的温度(取t0=100℃)。因此E=K(t-100)/10·τ。等效硫化即如上式，在硫化温度与硫化时间互为因数关系下，可以得到等效硫化程度。
CAS号：
性质：橡胶制品硫化程度的深浅可用硫化效应来表示，硫化效应相等即等效硫化。即E=Iτ。式中，E为硫化效应；I为硫化强度；τ为硫化时间。硫化强度是胶料在某温度下，单位时间内达到的硫化程度，即I=K(t-t0)/10；式中，K为硫化温度系数(一般取K=2)；t为硫化温度；t0规定硫化效应用的温度(取t0=100℃)。因此E=K(t-100)/10·τ。等效硫化即如上式，在硫化温度与硫化时间互为因数关系下，可以得到等效硫化程度。