1) boron fiber
硼纤维
1.
Effect of liquid nitrile-butadiene rubber on mechanical properties of unidirectional boron fiber/epoxy resin composites;
橡胶改性对硼纤维/环氧单向复合材料力学性能的影响
2.
The failure of the interface in single boron fiber pull-out test was analyzed.
设计了一种单根硼纤维拔出试样制备方法,并测试了不同树脂基体的硼纤维/环氧复合材料的界面剪切强度;研究了单根硼纤维拔出界面破坏过程。
3.
A model of single boron fiber(B_f)pullout was described,and the distribution of shear stress at the interface of B_f/epoxy resin composites was studied.
采用单根硼纤维拔出模型分析了硼纤维拔出过程界面剪切应力的分布;同时设计了一种单纤维拔出试样制备方法,并测试了不同硼纤维/环氧复合材料界面抗剪强度。
2) boron filament
硼纤维
1.
Research on a new type composite of boron filament/epoxy resin results that the tensile strength, tensile modulus and compiessive strength seem to reach 3 704 MPa, 394 GPa and 6 900 MPa, respectively.
研制了一种新型硼纤维/环氧预浸料。
2.
This paper introduces the production method, properties and application of boron filaments.
本文介绍了硼纤维的生产方法、性能及应用。
3) boron fibre
硼纤维
1.
The effect of hot pressing on strength property and distribution character of Boron fibre were observed.
硼纤维的拉伸断裂由缺陷引发，其强度分布符合Ｗｅｉｂｕｌ分布函数。
4) boron nitride fiber
氮化硼纤维
1.
Preparation of boron nitride fiber by precursor method;
先驱体法制备氮化硼纤维的研究
5) titanium boride fiber
硼化钛纤维
6) cellubose borates
硼酸纤维素
补充资料：硼纤维
| 硼纤维 boron fibre 在金属丝上沉积硼而形成的无机纤维。通常用氢和三氯化硼在炽热的钨丝上反应，置换出无定形的硼沉积于钨丝表面获得。属脆性材料，抗拉强度约3500兆帕，弹性模量400吉帕，密度只有钢材的1／4，抗压缩性能好；在惰性气体中，高温性能良好；在空气中超过500℃时，强度显著降低。是良好的增强材料，可与金属、塑料或陶瓷复合，制成高温结构用复合材料。如硼／铝复合板材，其纤维体积含量达50％时，在增强方向上抗拉强度达1500兆帕，弹性模量200吉帕，密度为2.6克／厘米3。由于其高的比强度和比模量，在航空、航天和军工领域获得广泛应用。硼纤维活性大，在制作复合材料时易与基体相互作用，影响材料的使用，故通常在其上涂敷碳化硼、碳化硅等涂料，以提高其惰性。 |