1) potassium tantalate
钽酸钾
1.
A series of large size and high quality potassium tantalate(KTa3O)single crystals up to 31 mm×31 mm×40 mm,weighing as much as 247 g,were grown by the Czochralski method.
用提拉法生长出了一系列钽酸钾(KTaO3)晶体,其中最大可达31mm×31mm×40mm,质量为247g。
2) potassium fluotantalate
氟钽酸钾
1.
Nb2O5 liquor is added into the Ta2O5 to form standard solution,then carry out chromatographic separating on paper after series of treatment with potassium fluotantalate sample parent solution.
在五氧化二钽基体中加五氧化二铌配成标准溶液,与氟钽酸钾样品在相同条件下经系列处理后进行纸上色层分离,分离后与样品直接进行目视比色。
2.
Determinated micro-sulfur of potassium fluotantalate, Sensitivity of combustion-conductance method is 0.
用燃烧—电导法测定氟钽酸钾中微量硫的灵敏度为 0 。
3) K 2TaF 7
氟钽酸钾
1.
Investigation is made on lowering of Fe,Ni and Cr impurities content in K 2TaF 7 and sodium reduced Ta Powder.
对降低氟钽酸钾钠还原钽粉中铁、镍、铬杂质含量问题进行了研究 ,结果表明 :降低钽粉中铁、镍、铬含量的最根本办法是在液 -液钠还原过程中减少熔盐对还原设备的腐蚀 ,选择合适的熔盐体系及组成、降低还原起始温度以及先以一定的钠与稀释剂在反应罐中熔融 ,然后再加氟钽酸钾并使之熔融的操作方法等 ,均可使钽粉中的铁、镍、铬含量明显减少。
补充资料：钽酸钾
分子式：KTaO3
CAS号：
性质：白色粉末，不溶于水。熔点1370℃。单晶为电光晶体。介电常数4400。居里温度-269℃(4K)。透光范围0.4～6μm。折射率2.4(λ=0.633nm)。由氢氧化钽和碱液作用生成或由五氧化二钽和碳酸钾反应制取。单晶用提拉法或泡生法制取。用于制造光电调制器。
CAS号：
性质：白色粉末，不溶于水。熔点1370℃。单晶为电光晶体。介电常数4400。居里温度-269℃(4K)。透光范围0.4～6μm。折射率2.4(λ=0.633nm)。由氢氧化钽和碱液作用生成或由五氧化二钽和碳酸钾反应制取。单晶用提拉法或泡生法制取。用于制造光电调制器。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条