2) PTFE composite membrane material
聚四氟乙烯复合膜材料
3) hydrocarbon membrane modified by porous PTFE membrane
聚四氟乙烯改性型复合膜
4) PTFE composites
聚四氟乙烯复合材料
1.
Experimental results showed that the best tribological behavior of the CF/PTFE composites was obtained when the content of rare earth elements was 0.
3%时,炭纤维填充聚四氟乙烯复合材料的摩擦磨损性能最佳;在干摩擦条件下,表面处理炭纤维填充聚四氟乙烯复合材料的摩擦系数比未经处理炭纤维填充聚四氟乙烯复合材料的低,且其耐磨性较好;稀土处理使得复合材料的界面强韧性得到明显改善,从而提高了其摩擦磨损性能。
2.
Experimental results revealed that the friction properties of PTFE composites filled with surface treated carbon fibers were better than those of the composite filled with untreated carbon fibers,while RE surface treated carbon fiber reinforced.
结果表明：在干摩擦条件下,表面处理碳纤维填充聚四氟乙烯(CF/PTFE)复合材料的摩擦系数比未经处理碳纤维填充聚四氟乙烯复合材料的低,而稀土处理碳纤维填充聚四氟乙烯复合材料具有最低的摩擦系数。
3.
The friction and wear properties of graphite/PTFE composites filled with different content nano-SiC have been studied in this article.
考察了不同含量的纳米SiC对石墨/聚四氟乙烯复合材料摩擦磨损性能的影响,采用扫描电子显微镜分析了磨损表面,并探讨了其磨损机理。
6) PTFE membrane
聚四氟乙烯膜
1.
The moisture permeable abilities were tested by hot plate method at the temperature of 33 and 50 ℃, for a variety of fabrics with different density, materials, laminated fabric and PTFE membrane and so on.
采用恒温板测试法,测量了33℃和50℃条件下,不同紧度、不同材料、纳米粉体改性织物前后以及层压和聚四氟乙烯膜4组试样的透湿性能。
补充资料：聚四氟乙烯
| 聚四氟乙烯 polytetra fluoroethylene 四氟乙烯的聚合物 。英文缩写为  。 结构为。聚四氟乙烯的分子量较大 ， 一般在数百万左右 。 结晶度90％～96％，熔融温度为 307～342 ℃以上。由于氟原子稍大于氢所以相邻的 CF2 单元按锯齿形排列，使整个分子链呈扭曲的螺旋状，氟原子几乎覆盖了整个聚四氟乙烯的表面。聚四氟乙烯由单体四氟乙烯经自由基聚合而成。工业上采用悬浮聚合的方法。一般在水中进行，便于热的异出和温度控制。反应温度在40～80℃，反应压力 3～26大气压，引发剂可采用过氧化物或过硫酸盐等。 聚四氟乙烯称为塑料之王 ，具有优秀的力学性能，自润滑性质，耐高低温、抗化学腐蚀，耐候性，优异的电性能及耐辐照。广泛地用于原子能工业、国防、航天、电子、电器、化工、机械，作为耐高低温、耐腐蚀、绝缘材料，防粘涂料等。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条