2) anti-crease
抗皱
1.
Producing process of the comfortable worsted fabric with anti-crease and self-clean function;
抗皱自清洁舒适性精毛纺面料的生产
2.
Cotton fabric is first treated with sodium chloromethyl sulfonate (CMSA) and then with cationized chitosan (CC) in order to improve its anti-crease property.
采用氯甲基磺酸钠(CMSA)使棉织物阴离子化,然后与阳离子壳聚糖(CC)离子交联对棉织物进行抗皱整理。
3.
This text developed a multifunctional worsted fabric which has anti-crease,self-clean,bidirectional elastic and machine washable functions to meet with the market.
介绍了一种集抗皱、自洁、双向弹性、机可洗等多种功能于一身的精毛纺面料,并研究了生产该面料的后整理工艺,抗皱、自洁、机可洗等功能整理都要求烘干后再进行焙烘,而多次焙烘又会影响面料的弹性及手感,经过实验,合理解决了多种功能整理中的各项矛盾,生产的面料完全能达到机可洗及免烫产品的指标要求,同时又具有良好的经纬向弹性及防水防油性能。
4) crepe-weavelike wrinkle
绉纱型皱纹
5) anti-crease finishing
抗皱整理
1.
One-bath acid dyeing and anti-crease finishing of cotton fabrics;
棉织物酸性染料染色和抗皱整理一浴法
2.
Research on the anti-crease finishing of tussah fabrics with glyoxal finishing agent;
乙二醛整理剂对柞蚕丝织物抗皱整理的研究
3.
and time in the anti-crease finishing, and the optimum process was found for ramie blended fabrics according to the strength loss and elastic recovery angles (T+W).
对影响整理效果的树脂和催化剂用量、焙烘温度和时间等因素进行了试验,以强力损失和弹性回复角(T+W)指标为依据,找出了适合苎麻棉混纺织物抗皱整理的最佳工艺:树脂NDW100g/L、催化剂MgCl220g/L、纤维保护剂SVN20g/L,焙烘温度160℃,焙烘时间控制在3min,弹性回复角(T+W)可达265°,强力损失38。
6) crease-resistant finishing
抗皱整理
1.
Nano-ZnO is used as a catalyst for crease-resistant finishing of silk fabric with water-soluble polyurethane.
将纳米 ZnO(氧化锌)作为催化剂,应用于水溶性聚氨酯对丝绸的抗皱整理。
2.
Cotton fabric was treated with the mixture of glutaraldehyde and hydrolyzed starch in the crease-resistant finishing of the fabric.
采用戊二醛与水解淀粉对棉织物进行抗皱整理,通过正交试验,讨论戊二醛和催化剂用量、淀粉水解时间、焙烘温度和焙烘时间等因素对整理后棉织物折皱回复角、断裂强力保持率、白度的影响,得出最佳工艺方案:淀粉水解时间为90min,戊二醛的浓度为70g/L,催化剂浓度为25g/L,焙烘温度为140℃,焙烘时间为3min。
3.
Nano-SiO2 was used as the catalyst of amino-silicone elastomer for crease-resistant finishing of silk knitting fabric.
用纳米SiO2作为氨基硅酮弹性体的催化剂,对真丝针织物进行抗皱整理。