1) combination tannage
结合鞣
1.
In order to improve the hydrothermal stability of leather,two kinds of tanning agents with weak properties were used in combination tannage.
利用两种鞣性比较弱的鞣质进行结合鞣制,得到的成革的耐湿热稳定性大幅度提高,原因是在这两种鞣质之间形成了协同效应,即Synergistic Effect,这是提高成革稳定性的一个比较新型的研究理论体系。
2.
The effect of combination tannage were studied by measurin g the change of shrinkage temperature during tanning processes, which were perfo rmed with different dosages of three tanning agents in the same tanning order.
通过测定3种鞣剂在相同鞣制顺序不同用量下的鞣制过程中,皮或革收缩温度的变化对结合鞣制效果做了研究,并对鞣制后成革耐老化试验前后的物理机械性能做了测定,同时考查了不同复鞣剂和加脂剂对结合鞣制效果的影响。
3.
The combination tannage of genipin with mimosa, quebracho, chestnut and aluminum salts was investigated based on the study of reaction prop erties of genipin and collagen.
在前期对京尼平(genipin)与皮胶原反应性研究的基础上,进一步考察了其与缩合类的荆树皮栲胶、水解类的栗木栲胶和铝盐的结合鞣时,各种鞣剂的用量和使用先后顺序对皮粉湿热稳定性的影响。
2) combination tanning
结合鞣
1.
Meanwhile,the modification approaches of vegetable tannin extracts for the purpose of combination tanning are described.
本文对各种以栲胶为基础的结合鞣法进行了综述,阐述了结合鞣的反应机理、工艺过程。
2.
It was summarized that the research progress on Techniques of chrome-free and chrome- reduced combination tanning at home and abroad.
对国内外无铬少铬结合鞣的研究动态进行了综述。
3.
The combination tanning method by vegetable tannin-modified glutaraldehyde was introduced, including optimization of pretreatment and retanning by modified glutaraldehyde.
介绍了植物鞣剂与改性戊二醛结合鞣法,包括预处理方案的优化和改性戊二醛复鞣方案的优化。
3) combined tanning
结合鞣
1.
Comparing the tanning effects of above four chrome free tanning agents,NBT-501 and THPS were selected for further combined tanning process.
确定了2种丙烯酸树脂(NBT-501、NBT-502)和2种四羟甲基盐(THPC、THPS)无铬鞣剂的单独鞣制工艺,通过对上述4种材料的鞣制效果进行对比,优选出NBT-502和THPS进行结合鞣制,并进一步研究了NBT-502和THPS结合鞣的工艺,使皮革的收缩温度达到85℃,实现无铬、无金属鞣制皮革。
4) combination tannage
结合鞣法
1.
In this paper,combination tannage of vegetable tannin and syntan had been studied.
本文研究植物鞣剂──合成鞣剂结合鞣法。
5) combined tannin
结合鞣质
6) combination tanned leather
结合鞣革
补充资料：结合鞣法
分子式：
CAS号：
性质： 用两种或两种以上鞣剂作主鞣剂，同时或先后鞣制的方法。成革兼有所用鞣剂的长处或得到增益作用。例如植物鞣革耐汗性差，收缩温度一般在75～80℃；铝鞣革不耐水，收缩温度只有70～75℃。但植-铝结合鞣革性质稳定，收缩温度可达100℃以上，耐汗性好。又如铬-植结合鞣鞋面革不易松面，丰满性好；铬-植结合鞣的鞋底革富有弹性，耐磨性也比单用植鞣法有较大提高。
CAS号：
性质： 用两种或两种以上鞣剂作主鞣剂，同时或先后鞣制的方法。成革兼有所用鞣剂的长处或得到增益作用。例如植物鞣革耐汗性差，收缩温度一般在75～80℃；铝鞣革不耐水，收缩温度只有70～75℃。但植-铝结合鞣革性质稳定，收缩温度可达100℃以上，耐汗性好。又如铬-植结合鞣鞋面革不易松面，丰满性好；铬-植结合鞣的鞋底革富有弹性，耐磨性也比单用植鞣法有较大提高。