1) polydivinylbenzene
[,pɔlidai,vinil'benzi:n]
聚二乙烯基苯
1.
A polydivinylbenzene/poly(methyl acrylate) interpenetrating polymer network (PDVB-PMA IPN) was synthesized.
采用分步聚合法合成了两网质量比不同,第二网交联度均为30%的聚二乙烯基苯/聚丙烯酸甲酯互穿聚合物网络(PDVB-PMA IPN),将它们分别用20%的NaOH/甲醇溶液碱解,合成了一网疏水、一网亲水的聚二乙烯基苯/聚丙烯酸互穿聚合物网络(PDVB-PAA IPN)。
2.
Theophylline molecules imprinted and non-imprinted interpenetrating polymer networks composed of sulfonated polydivinylbenzene and polydivinylbenzene(PDVB-SO3H/PDVB IPNs) are synthesized by suspension polymerization of divinylbenzene swelling into sulfonated polydivinylbenzene beads with the existence of porogens.
将工业二乙烯基苯和致孔剂溶胀到磺化聚二乙烯基苯树脂球中,通过悬浮聚合合成了茶碱分子印迹和非分子印迹的大孔磺化聚二乙烯基苯/聚二乙烯基苯互穿聚合物网络(PDVB-SO3H/PDVB IPN)珠体,测定了2种IPN的结构及其对茶碱的吸附性能。
3.
Theophylline molecules imprinted and non-imprinted interpenetrating polymer networks composed of sulfonated polydivinylbenzene and polydivinylbenzene (PDVB-SO3H/PDVB IPNs) were synthesized by suspension polymerization of divinylbenzene swelling into sulfonated polydivinylbenzene beads with the existence of porogens.
将工业二乙烯基苯和致孔剂溶胀到磺化聚二乙烯基苯树脂球中,通过悬浮聚合合成了茶碱分子印迹和非分子印迹的大孔磺化聚二乙烯基苯/聚二乙烯基苯互穿聚合物网络(PDVB-SO3H/PDVBIPN)珠体,考察了反应时间、分散剂和吸附介质对其吸附性能的影响。
2) polystyrene-divinylbenze
聚苯乙烯-二乙烯基苯
1.
Irradiation grafting reaction of polystyrene-divinylbenze with acrylonitrile;
交联聚苯乙烯-二乙烯基苯与丙烯腈的辐照接枝
2.
Acrylonitrile was grafted onto pre-irradiated polystyrene-divinylbenze resin in air,and the target functional group was introduced through amidoximation reaction.
以聚苯乙烯-二乙烯基苯(SDB)树脂颗粒为基体,通过预辐照接枝聚合途径在空气气氛中接枝丙烯腈(AN),然后用盐酸羟胺作功能化处理而引入胺肟基团。
3) poly(divinylbenzene/styrene)
聚(二乙烯基苯/苯乙烯)
4) (methacrylic acid-styrene-divinylbenzene) copolymer
(甲基丙烯酸-苯乙烯-二乙烯基苯)共聚物
5) Benzene, diethenyl-, polymer with ethenylethylbenzene
二乙烯基苯与乙烯基乙苯的聚合物
6) Benzene, diethenyl-, polymer with ethenylbenzene and ethenylethylbenzene, chloromethylated, trimethylamine-quaternized, hydroxide
二乙烯基苯、苯乙烯、乙烯基乙苯的聚合物
补充资料：乙烯基苯
分子量 104．14
性质 无色透明油状液化密度0.9074 g／cm3。熔点-31℃。沸点146℃。闪点31．3℃。自燃点490℃。能溶于醇及醚，难溶于水。遇明火极易燃烧。受热、曝光或存在过氧化物催化剂时，极易聚合放热导致爆炸。与氯磺酸、发烟硫酸、浓硫酸反应剧烈，有爆炸危险。有毒，对人体皮肤、眼和呼吸系统有刺激性。空气中最高容许浓度为100ppm。爆炸极限为1．1-6．1%。
应用 是生产合成树脂、塑料和合成橡胶等合成高分子材料的重要有机化工原料。经本体聚合可制得通用塑料聚苯乙烯，广泛用于制备各类仪表、电讯的壳体，纱管，线团芯。
性质 无色透明油状液化密度0.9074 g／cm3。熔点-31℃。沸点146℃。闪点31．3℃。自燃点490℃。能溶于醇及醚，难溶于水。遇明火极易燃烧。受热、曝光或存在过氧化物催化剂时，极易聚合放热导致爆炸。与氯磺酸、发烟硫酸、浓硫酸反应剧烈，有爆炸危险。有毒，对人体皮肤、眼和呼吸系统有刺激性。空气中最高容许浓度为100ppm。爆炸极限为1．1-6．1%。
应用 是生产合成树脂、塑料和合成橡胶等合成高分子材料的重要有机化工原料。经本体聚合可制得通用塑料聚苯乙烯，广泛用于制备各类仪表、电讯的壳体，纱管，线团芯。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。