1) spraying distance
喷涂距离
1.
Thermal barrier coatings were prepared by plasma spraying in different spraying distance,and through the tensile test of coating,XRD and SEM analysis,the influnce law of spraying distance on tensile strength(σ) of coating was investigated.
用等离子喷涂方法,在不同的喷涂距离(d)下制备出ZrO2陶瓷涂层,通过涂层的拉伸实验、X射线衍射和扫描电镜分析,研究了喷涂距离对涂层拉伸强度(σ)的影响规律。
2.
The effect of the spraying distance on the crystallization,surface morphology,electrical and optical properties of the films was investigated by X-ray diffraction,field emission scanning electron microscope,resistance tester and ultraviolet-visible spectrometer.
采用X射线衍射、场发射扫描电子显微镜、电阻仪、紫外-可见光谱仪等研究了喷涂距离(输入TiCl4管道末端到基板之间的距离)对沉积的TiN薄膜的结晶性能和表面形貌,以及薄膜的电学性能和光学性能的影响。
3.
During the wire electrical explosion,the coating feature is influenced by process variables such as input energy density,spraying distance.
为研究电爆喷涂工艺中输入能量密度及喷涂距离与喷涂效果之间的关系,利用高压电场中金属丝段与电极非接触电爆设备,通过改变金属丝长度和电极间电压进行系列金属丝段电爆喷涂试验,获得熔融粒子涂层、固态颗粒堆积涂层、气相沉积涂层及气相堆积涂层共4种涂层效果,其中熔融粒子涂层和气相沉积涂层具有工程应用价值。
2) spray distance
喷涂距离
1.
Experimental results indicate that proper spray distance,relatively larger arc-plasma current and voltage,comparatively lower powder feed rate can increase the microhardness and decrease the porosity of the coating;and thereby the optimized parameters are obtained.
通过正交试验方案分析了等离子喷涂主要工艺参数,即等离子弧电流、等离子弧电压、送粉率、喷涂距离,对NiCrBSi/Al2O3-TiO2涂层的显微硬度及孔隙度的影响,结合用光学显微镜对涂层显微形貌的观察和分析,得出的最佳工艺参数为电流I=600 A,电压U=55 V,送粉率F=15 g/min,喷涂距离S=10 cm;并且表明,采用适当的喷涂距离、较大的等离子弧电流和电压、较低的送粉率,可以提高涂层的显微硬度并降低其孔隙度。
2.
Hydroxyapatite (HA) coatings on Ti-6Al-4V substrate were prepared by atmospheric plasmasprating method under a variety of spray distances and spray powers.
本文以Ｔｉ－６Ａｌ－４Ｖ合金为基体材料，采用等离子喷涂方法，在不同喷涂距离和喷涂功率下制备羟基磷灰石（ＨＡ）涂层，研究喷涂距离和喷涂功率这两个重要的喷涂参数对涂层结构和组成的影响。
3) centrifugal painting
离心喷涂
1.
The structure and working principle of hot melting road line markers with centrifugal painting are introduced.
介绍了离心喷涂式热熔道路标线划线机的结构、工作原理,分析了该机型与广泛使用的刮板式划线机相比所具有的优势及不足,并就其最适宜的各种应用工况进行了论述。
4) Distance of jet openings
喷口距离
5) Spray distance
喷射距离
1.
Corrosion resistant of polyacrylate waterproof materials in the solution of chloride,sulfate and alkali was studied in static immersion,and relation between swelling ratio and anti-erosion of polymers formed by different initiators of spray distance and mass ratio was investigated.
通过溶胀度的测定,研究了不同喷射距离及不同质量分数引发剂所形成的聚合物溶胀度变化与抗侵蚀性关系。
6) plasma spraying
等离子喷涂
1.
Microstructure and property of Al_(65)Cu_(23)Fe_(12) coating prepared by plasma spraying;
等离子喷涂Al_(65)Cu_(23)Fe_(12)涂层的组织与性能研究
2.
Forming characters of Fe_(80)P_(13)C_7 amorphous coating fabricated by bar material plasma spraying;
棒材等离子喷涂法制备Fe_(80)P_(13)C_7非晶态合金涂层的成形特征
3.
Studying of Reactive Plasma Spraying TiN-Al_3Ti-Al Composite Coating;
反应等离子喷涂TiN-Al_3Ti-Al复相陶瓷涂层的研究
补充资料：爆炸喷涂层
爆炸喷涂层
detonation coating
嗽烧涂材爆炸喷涂层detonatio;1 eoati眼利用气体献爆炸能加热喷涂材料，并利用燃气高速冲击波将啧料喷向零件表面形成的涂层。 工艺和原理定量地‘将可燃气体(如乙炔、卜丙烷、氢气等，和氧气称空气输入枪膛内，再输入的涂料粉末，在火花塞点火的同时输入氮气，此时内发生爆炸，完成一个循环过程。爆炸循环的周2一8次/so氮气流的作用是在爆炸时保护阀门不响，并将枪膛内的残余燃气清理出去，为下一次爆准备。枪口与被涂零件之间的距离约为5一巧cm。 混合气体爆炸时形成高温和冲击波，由于枪膛闭状态，冲击波集中到非常小的面积上，使之进一强氧一乙炔的爆炸，冲击波的速度可达3000m/*从枪口喷出的气流速度实际上可达1200m/。。由流速度使粉末得到加速达800m/s。在爆炸的同时末被加热到很高温度，当动能转变为热能时，温度步提高，达到4000℃。这时粉末材料包括氧化铝(205了C)、碳化钨嘴卉2800℃)等高熔点化合物都于熔点以上的状态。在这种情况下，粉禾由原来的形变为扁平形，并以高速度喷涂在零艇，形成薄状结构嵌入零件表面。由于粉末材料i与基体产生显接作用、使之具有冶金及机械结合的特征，因此涂有很高的结合强度和低的孔隙率。 特性和应用爆炸喷涂工艺及涂层性能与其他涂相比有许多优点。以碳化钨涂层材料为例，与热喷较优良的等离子喷涂的工艺势数和涂层性能对比见 等离子喷涂与爆炸喷涂特性比较叙量膛为影作嗡越创戮煞料为封步加而气粉一点处圆层悍具 于笠容J一佑内版召石喷中。