1) inorganic sol-gel method
无机溶胶-凝胶法
1.
The V2O5 gelatin film was prepared by inorganic sol-gel method from V2O4 powder and was dried in first annealing operation,then,the dry V2O5 film was annealed in vacuum quartz pipe at 450 ℃ and 480 ℃ respectively,so the VO2 thin film was obtained.
以V2O4粉末为原料,采用无机溶胶-凝胶法在玻璃衬底上制备了V2O5干凝胶膜。
2.
Vanadium oxide(VO_2) thin films were prepared by inorganic sol-gel method.
应用无机溶胶-凝胶法在玻璃基片上制得VO2薄膜样品,并研究了真空热处理温度和掺杂对VO2薄膜光电性能的影响。
3.
An inorganic sol-gel method was developed to synthesize Zr~ 4+ doped vanadium oxide (VO_X) phase transition thin films by using V_2O_5 powders and Zr(NO_3)4.
以V2O5和Zr(NO3)4·5H2O为原料,采用无机溶胶-凝胶法制备了掺Zr4+的VOX(2≤X≤2·5)相变薄膜。
2) inorganic sol-gel
无机盐溶胶-凝胶法
3) inorganic-sol-gel (ISG) method
无机盐溶胶-凝胶法(ISG)
4) sol gel process/inorganic membrane
溶胶-凝胶法/无机膜
5) inorganic-solgel method
无机盐溶胶凝胶法
6) inorganic chelating sol-gel method
无机络合溶胶-凝胶法
补充资料：溶胶-凝胶法
分子式：
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。
CAS号：
性质：一种用于制取无机固体材料和器件的方法。无机固体化合物和无机材料通常是利用高温固相反应制备，但是，一般地说，高温固相反应得到固体产物的均匀性较差，反应所需的温度较高，产物的料理论基础和形貌也无法控制。溶胶-凝胶方法利用前体物（如醇盐或无机盐）将反应物在分子的尺度上均匀混合，经溶胶和凝胶过程使之转变为固体；由于固体凝胶中反应物是在分子水平上均匀混合，避免了固相反应扩散过程，使反应可以在较低的温度下进行，还可以根据需要将凝胶成型，再经热处理得到具有一定形状的材料和器件。利用溶胶-凝胶方法可以制备出各种形态的材料，如薄膜、纤维、块体或粉末等。近年来，溶胶-凝胶方法在很多领域中得到了广泛应用，特别是在陶瓷材料和器件上制造中的应用，得到了多种均匀、具有特定微结构和性能的固体材料。