1) SiCp/Al composites
SiCp/Al复合材料
1.
Preparation of high volume fraction SiCp/Al composites for electronic packaging;
电子封装用高体积分数SiCp／Al复合材料的制备
2.
Anti-corrosion properties of electroless nickel coating on SiCp/Al composites;
SiCp/Al复合材料化学镀镍耐蚀性研究
3.
An Application of Focusing Probe in SiCp/Al Composites′ Nondestructive Testing;
聚焦换能器在SiCp/Al复合材料超声无损检测中的应用
2) SiCp/Al composite
SiCp/Al复合材料
1.
Oxidation behavior of silicon carbide particales and its influence on the mechanical performance in SiCp/Al composites;
SiCp的氧化行为及其对SiCp/Al复合材料力学性能的影响
2.
Effect of heat treatment on tensile deformation behavior of SiCp/Al composites
热处理对SiCp/Al复合材料拉伸变形行为的影响
3.
42m·s-1,of the SiCp/Al composites and gray cast iron(HT250) were investigated using a block-on-ring test at room temperature under dry sliding against a semi-metallic brake pad.
在M-200型环块式磨损试验机上研究了SiCp/Al复合材料、灰铸铁(HT250)分别与半金属刹车材料配副的干摩擦磨损性能。
3) SiC_p/Al composites
SiCp/Al复合材料
1.
The high volume fraction SiC_p/Al composites were fabricated by vacuum-adjustable pressure infiltration process.
采用真空变压力浸渗法制备高体积分数SiCp/Al复合材料。
2.
Under the condition of different particle dimension, different matrix, different preheat treatment and different thermal cycling times, cumulative residual strain ε_(cr) of high volume SiC_p/Al composites was studied during the course of thermal cycle.
研究了高比例大尺寸SiCp/Al复合材料于不同颗粒尺寸、基体、预处理类型及热循环次数情况下在热循环过程中的累积残余应变(εcr)。
3.
SiC_p/Al composites was fabricated by melt stirring casting and the influence of predistribution of SiC particles on its microstructure was investigated.
采用液态搅拌法制备SiCp/ZL10 5复合材料 ,研究预分散措施对SiCp/Al复合材料微观组织均匀性的影响规律。
4) SiC_p/Al composite
SiCp/Al复合材料
1.
The jointing performance of SiC_p/Al composite with LD2 by the friction welding was studied,the microstructure of the bonded joint was examined,and the microhardness of the weld beam was measured.
采用摩擦焊方法对SiCp/Al复合材料与LD2进行连接。
2.
0Ni solder was used to solder SiC_p/Al composite substrate with two types of electroless Ni(P) layers.
0Ni焊料钎焊两种化学镀Ni(P)后的SiCp/Al复合材料。
3.
Study on Preparation and Impact Property of High Volume Fraction SiC_p/Al Composites;
本文以无压浸渗工艺制备的高体积分数SiCp/Al复合材料为研究对象,对液态Al合金熔体浸渗SiC颗粒多孔体的浸渗过程、复合材料的微观组织和界面特性进行了理论与实验研究;利用西北工业大学结构和强度国家专业实验室研制的分段式Hopkinson压杆系统开展了增强相体积分数为65%的SiCp/Al复合材料的高应变率压缩行为和变形机制的研究。
5) SiC p/Al composites
SiCp/Al复合材料
1.
Through the cutting experiments in which SiC p/Al composites are machined with CVD thin film diamond coated tools, the influences of cutting parameters, tool materials, geometrical parameters of tools and workpiece materials on the tool wear are studied.
通过用CVD金刚石薄膜涂层刀具切削加工SiC颗粒增强铝基复合材料的试验 ,研究了切削参数、刀具材料、刀具几何参数和工件材料对CVD金刚石薄膜涂层刀具磨损的影响规律 ,同时研究了SiCp/Al复合材料的切削加工性能。
6) SiCp/Al MMCs
SiCp/Al基复合材料
1.
In order to analyze the weldability of SiC particle reinforced aluminum metal matrix composites(SiCp/Al MMCs),plasma arc in-situ welding of SiCp/Al MMCs was carried out using argon-nitrogen mixture as plasma gas with Ti-Mg mixed powder as in-situ material.
为分析SiCp/Al基复合材料的焊接性,以Ti-Mg混合粉末作为填充材料,采用氮氩混合等离子气体对SiCp/Al基复合材料进行等离子弧原位焊接。
2.
Plasma arc "in-situ" welding of SiCp/Al MMCs were carried out using argon-nitrogen mixture as plasma gases with Ti-Ni alloying as "in-situ" material.
以Ti-Ni合金作为填加材料,采用氮氩混合等离子气对SiCp/Al基复合材料进行等离子弧原位焊接。
3.
In this paper,SiCp/Al MMCs were selected as research objects,and process and mechanism of SiCp/6061Al MMCs by plasma arc welding(Ar and N2 as ionized gas, Ar as fielded gas) were systematically studied.
研究表明填加Al-Si-Ti-Ni合金对SiCp/Al基复合材料进行等离子弧原位焊接,填加材料中Ti含量为5%时,可以有效抑制有害相Al_4C_3的生成,得到的焊缝组织较为致密,没有气孔、微观裂纹等缺陷,接头强度较之不加填充材料时有较大提高,达到226MPa,提高了接头的力学性能。
补充资料：复合材料的复合效应
复合材料的复合效应
composition effect of composite materials
复合材料的复合效应Composition effeet of Com-Posite materials复合材料特有的一种效应，包括线性效应和非线性效应两类。 线性效应包括平均效应、平行效应、相补效应和相抵效应。例如常用于估算增强体与基体在不同体积分数情况下性能的混合率，即 Pc一巧几+VmPm式中Pc为复合材料的某一性质，乃、几分别为增强体和基体的这种性质，VR、Vm则分别是两者的体积分数。这就是基于平均效应上的典型事例。另外关于相补效应和相抵效应，它们常常是共同存在的。显然，相补效应是希望得到的而相抵效应要尽可能避免，这个可通过设计来实现。 非线性效应包括乘积效应、系统效应、诱导效应和共振效应、其中有的己经被认识和利用，并为功能复合材料的设计提供了很大自由度;而有的效应则尚未被充分地认识和利用。乘积效应即已被用于设计功能复合材料。如把一种具有两种性能互相转换的功能材料X/y(如压力/磁场换能材料)和另一种Y/Z的换能材料(如磁场/电阻换能材料)复合起来，其效果是(X/D·(Y/Z)二X/Z，即变成压力/电阻换能的新材料。这样的组合可以非常广泛(见表)。系统效应的机理尚不很清楚，但在实际现象中已经发现这种效应的存在。例如交替迭层镀膜的硬度远大于原来各单一镀膜的硬度和按线性棍合率估算的数值，说明组成了复合系统才能出现的性质。诱导行为已经在很多实验中发现，同时这种效应也在复合材料的乘积效应┌──────┬──────┬──────────┐│甲相性质 │乙相性质 │复合后的乘积性质 ││ X/y │ Y/Z │沙到豹·(Y/公一义您 │├──────┼──────┼──────────┤│压磁效应 │磁阻效应 │压敏电阻效应 │├──────┼──────┼──────────┤│压磁效应 │磁电效应 │压电效应 │├──────┼──────┼──────────┤│压电效应 │场致发光效应│压力发光效应 │├──────┼──────┼──────────┤│磁致伸缩效应│压阻效应 │磁阻效应 │├──────┼──────┼──────────┤│光导效应 │电致效应 │光致伸缩 │├──────┼──────┼──────────┤│闪烁效应 │光导效应 │辐射诱导导电 │├──────┼──────┼──────────┤│热致变形效应│压敏电阻效应│热敏电阻效应 │└──────┴──────┴──────────┘复合材料界面的两侧发现，如诱导结晶或取向，但是尚未能利用这种效应来主动地设计复合材料。两个相邻的物体在一定的条件下会产生机械的或电、磁的共振，这是熟知的物理行为。复合材料是多种材料的组合，如果加以有目的性的设计，肯定可利用这种共振效应，但是目前尚未加以研究。(吴人洁)