1) amine terminated polyether
端氨基聚醚
1.
Research progress of preparing amine terminated polyether based on the leaving group method
离去基团法制备端氨基聚醚的研究进展
2.
The characteristic of reacting amine terminated polyether (ATPE) to polyisocyanate, the property profile of polyurea structure is described firstly.
首先论述了端氨基聚醚 (ATPE)与多异氰酸酯的反应特性 ,以及制成的聚脲结构的性能特征。
3.
In this paper, the key component of Polyurea coating,Amine terminated Polyether(ATPE) was synthesized , the processing parameters of Polyurea coating was determined and the Polyurea coating used in the oil-pipeline was prepared.
本论文主要研究了聚脲涂料的关键组分——端氨基聚醚的实验室合成方法及聚脲涂料在管道防腐大修方面的应用，并针对管道防腐大修的要求对聚脲涂料与金属的附着力和聚脲涂料的阴极剥离性能进行了深入的研究，并最终制备了满足管道防腐大修用性能要求的可在工程上实际应用的聚脲涂料。
2) polyoxyalkyleneamine
端氨基聚醚
1.
A novel polyoxyalkyleneamine with high reaction activity used in sprayed polyurea elastomer was synthesized by the reaction of amino-crotonic acid ester.
采用氨基丁酸酯法合成了可用于喷涂聚脲弹性体的高活性端氨基聚醚。
2.
Some novel polyoxyalkyleneamine with specific structure and high reaction activity used in sprayed polyurea elastomer have been synthesized.
用一种新的方法合成了具有特定结构的高活性端氨基聚醚,首先将双乙烯酮与聚醚反应生成乙酰乙酸酯类,再将乙酰乙酸酯类与胺反应生成具有氨基丁烯酸酯基团的端氨基聚醚。
3) amine-terminated polyether
端氨基聚醚
1.
A novel amine-terminated polyether(ATPE) was synthesized with two steps.
使用双金属氰化物催化剂对高活性聚醚进行封端反应,得到聚醚末端带有一定数量环氧氯丙烷的邻氯醇聚醚,然后再和氨水反应能得到端氨基聚醚。
2.
Two dithiocarbamate-type flocculants,DTC-1 and DTC-2,were synthesized with two amine-terminated polyether compounds,Jeffamine-T403 and Jeffamine-D230.
用2种端氨基聚醚化合物Jeffamine-T403和Jeffamine-D230作原料分别合成了二硫代氨基甲酸盐型絮凝剂DTC-1和DTC-2,利用红外光谱分析,确认了产物分子的结构。
4) aliphatic amine-terminated polyether
端脂肪氨基聚醚
1.
Research on environmental resistance of aliphatic amine-terminated polyether/ epoxy resin coatings;
端脂肪氨基聚醚/环氧树脂涂料的耐环境性能研究
5) aromatic amino-terminated polyether
端芳香氨基聚醚
1.
A kind of advanced adhesives with high performance was based on epoxy resin and aromatic amino-terminated polyether (ATPE).
用端芳香氨基聚醚(ATPE)与E-44环氧树脂组成了高强、高韧的胶粘剂。
6) amine-terminated PEG
双端氨基聚醚
补充资料：端氨基聚醚多元醇
分子式：
CAS号：
性质：末端全部被氨基(-NH2)取代的聚醚多元醇称为端氨基聚醚多元醇。常温下为透明黏稠液体，同异氰酸酯有高的反应活性，能使聚氨酯成型在室温进行。其制法是含伯羟基和仲羟基的聚醚多元醇同氨在氢和氢/脱氢催化剂存在下反应而制得。用于制造快速固化的反应注塑成型聚脲弹性体等。
CAS号：
性质：末端全部被氨基(-NH2)取代的聚醚多元醇称为端氨基聚醚多元醇。常温下为透明黏稠液体，同异氰酸酯有高的反应活性，能使聚氨酯成型在室温进行。其制法是含伯羟基和仲羟基的聚醚多元醇同氨在氢和氢/脱氢催化剂存在下反应而制得。用于制造快速固化的反应注塑成型聚脲弹性体等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。