1) reclaimed rubber
再生胶
1.
Preparation of polyvinylchloride/reclaimed rubber/vulcanizedrubber powder blended thermoplastic elastomer;
动态硫化聚氯乙烯/再生胶/硫化胶粉共混型热塑性弹性体的研制
2.
Analyzed the present status and development trend of reclaimed rubber industry domestic and abroad, and put forward the development idea.
分析国内外再生胶行业的现状与发展趋势,对我国废旧橡胶综合开发利用提出发展思路、措施和建议。
3.
The influence of the amount of devulcanizing agent and compounding ingredients, reclaiming time and reclaiming temperature on the performance of reclaimed rubber was discussed in detail.
用自制的De link再生剂对废旧胎面胶的再生工艺进行实验研究 ,分析再生剂和配合剂的用量及再生时间和再生温度对再生胶性能的影响 。
2) reclaim
[英][rɪ'kleɪm] [美][rɪ'klem]
再生胶
1.
Application of reclaim in sidewall compound of PCR tire
再生胶在轿车子午线轮胎胎侧胶中的应用
2.
The production of reclaim by microwave devulcanizing process at home and abroad was related.
叙述了国内外用微波脱硫法生产再生胶的情况。
3.
An experimental study was made on the reclaim process of various vulcanizates with the microwave radiation.
结果表明，炭黑填充硫黄硫化的极性和非极性废橡胶都可采用微波辐射再生，在频率为９１５ＭＨｚ的微波场中，粒径为３—５ｍｍ的废胶约辐射５ｍｉｎ，即可充分破坏硫黄文联网络，从而获得性能十分接近原胶的再生胶。
3) Regenerated rubber
再生胶
1.
The waste butyl rubber can be mainly reclaimed by the use of regenerated rubber and waste rubber powder or activated waste rubber powder.
再生胶、胶粉及活化胶粉是废丁基橡胶回收利用的主要途径和方法,其中再生胶应用效果最好。
2.
The main method and developing trend of scrap rubber reclaiming and recycling were introduced in this paper,including the directly reuse of scrap rubber,recycling via grinding to rubber powder,de-sulphuring to produce regenerated rubber,pyrolysis and combustion.
综述了目前废旧橡胶回收和循环利用的现状和发展趋势,主要包括废旧橡胶的直接利用、磨成胶粉后利用、通过再生胶重新利用、热分解后利用以及燃烧等。
4) reclaimed IIR
IIR再生胶
1.
The application of filler Austin Black and reclaimed IIR in inner liner compound of TBR tire was investigated.
试验研究填充剂Austin Black和IIR再生胶在全钢载重子午线轮胎气密层中的应用效果。
5) renewable powder
再生胶粉
1.
In order to broaden the application of the powder, the paper mainly from three aspects of the fine,superfine powder production,the powder surface modification, the production of renewable powder expounded on the application of powder to broaden the ways and feasibility.
为了拓宽胶粉的应用,主要从精细和超细胶粉的生产、胶粉的表面改性、再生胶粉的生产三个方面阐述了拓宽胶粉应用的途径和可行性。
6) rebirth silica gel
再生硅胶
1.
This paper explores a method of adopting household-use microwave heating the rebirth silica gel, and ex- amines the relation between power of microwave, time and rebirth silica gel quality.
采用家用微波炉加热再生硅胶的方法,考查了微波功率、时间及再生硅胶质量之间的关系,结果表明,微波加热干燥硅胶500g,功率为60%时,只需10分钟,颜色由粉红色变为深蓝色。
补充资料：再生胶
以橡胶制品生产中产生的已硫化的边角废料为原料，加工成有一定可塑度、能重新使用的橡胶。随所用废胶不同，再生胶可分为外胎类、内胎类、胶鞋类等。再生胶能部分地代替生胶用于橡胶制品，以节约生胶及炭黑用量，也有利于改善加工和橡胶制品的某些性能。再生过程是废胶在增塑剂（软化剂和活化剂）、氧、热和机械剪切的综合作用下使硫化橡胶的部分分子链和交联点断裂的过程。软化剂起膨胀和增塑作用，常用的有煤焦油、松焦油、石油系软化剂、裂化渣油。活化剂能缩短再生时间，减少软化剂用量。常用的活化剂为芳香族硫醇及其锌盐和芳香族二硫化物。
生产过程分为粉碎、再生（脱硫）和精炼三个工序。粉碎工序包括废胶的切胶、洗涤、粉碎，去除金属和纤维。精炼工序包括捏炼、滤胶和精炼等。再生工序常用油法或水油法。油法是将废胶经拌油送进卧式蒸汽罐中加热再生。水油法是在带有搅拌器和高压蒸汽夹套的罐中，装入温水、软化剂、活化剂和胶粉，在搅拌下加热再生。水油法产品质量较好，生产效率较高，是目前再生胶的主要生产方法。一些特殊橡胶、如丁腈橡胶、丁基橡胶、硅橡胶、氟橡胶等，另有专门的再生方法，不能与通用橡胶混杂在一起。除上述传统再生方法外，正在开发将废胶冷冻粉碎,制成不同颗粒大小的橡胶粉,直接用作橡胶的填料，这是利用废胶的一种新途径。
生产过程分为粉碎、再生（脱硫）和精炼三个工序。粉碎工序包括废胶的切胶、洗涤、粉碎，去除金属和纤维。精炼工序包括捏炼、滤胶和精炼等。再生工序常用油法或水油法。油法是将废胶经拌油送进卧式蒸汽罐中加热再生。水油法是在带有搅拌器和高压蒸汽夹套的罐中，装入温水、软化剂、活化剂和胶粉，在搅拌下加热再生。水油法产品质量较好，生产效率较高，是目前再生胶的主要生产方法。一些特殊橡胶、如丁腈橡胶、丁基橡胶、硅橡胶、氟橡胶等，另有专门的再生方法，不能与通用橡胶混杂在一起。除上述传统再生方法外，正在开发将废胶冷冻粉碎,制成不同颗粒大小的橡胶粉,直接用作橡胶的填料，这是利用废胶的一种新途径。