1) hydrothermal
[英][,haidrə'θə:məl] [美][,haɪdrə'θɝmḷ]
水热
1.
PZT nanoparticles synthesized by sol-hydrothermal method and properties;
溶胶-水热法合成PZT纳米粉体及性能研究
2.
Influence of Hydrothermal Temperature on Structural and Microstructural Properties of Boehmite;
水热温度对水合氧化铝相结构及微观形貌的影响
3.
The preperation of core-shell nanopowder material by one-step hydrothermal method;
一步水热法制备核壳型纳米粉体研究
2) hydrothermal method
水热
1.
Application of hydrothermal method in PbS nanocrystals preparation;
水热法在纳米硫化铅制备中的应用
2.
The Mo-V-Te-La catalysts were prepared by hydrothermal method and then dried through microwave heat method.
采用水热合成法并使用微波加热干燥制备了Mo-V-Te-La复合金属氧化物催化剂。
3.
The zinc phosphate has been synthesized by hydrothermal method in the presence of Zn (NO 3) 2·6H 2O,NaBr, H 3PO 4 and NaOH at 70 ℃ in 14 h.
用水热方法 ,以 Zn(NO3) 2 · 6 H2 O、Na Br、H3PO4 、Na OH为反应原料 ,于 70℃反应 14 h合成磷酸锌。
3) hydrothermal synthesis
水热
1.
Effect of synthesis conditions and the addition of triethanolamine on the hydrothermal synthesis of TS-1 and its properties;
合成条件及添加三乙醇胺对水热法合成TS-1分子筛及其性能的影响
2.
The hydrothermal synthesis method of abio-nanoparticles and it's extending method;
无机纳米材料的水热合成及其衍生方法
4) hydrothermal treatment
水热
1.
Different hydrothermal treatment methods, including hydrothermal treatment at low temperature, at high temperature, in NaOH solution and hydrothermal treatment after seeding as well, were used to treat the magnesium hydroxide powder.
采用低温水热、高温水热、氢氧化钠环境水热、引入晶种水热等不同水热工艺制备出超细氢氧化镁粉体。
2.
In the process of preparing magnesium oxysulfate whisker by hydrothermal treatment, the effects of magnesium sulfate, match of raw materials, reaction time, reaction temperature and stirring velocity on whi.
本课题在水热制备碱式硫酸镁晶须的研究中,讨论了硫酸镁浓度(c)、原料配比、反应时间(t_r)、反应温度(T_r)以及搅拌速率(ν)等参数对产品形貌的影响;通过SEM、XRD、TG、BET等手段对晶须产品进行了表征,并结合碱式硫酸镁晶须结构、晶体生长理论对晶须的生长进行了探讨;通过添加有机酸的方法研究了增大晶须长径比的可能性;对于不同的原料体系进行了对比研究,探索研究简单适用的原料体系;对于不同的反应器进行了对比研究,对比了搅拌间歇反应器结合水热反应与定-转子反应器结合水热反应制备碱式硫酸镁晶须产品的不同。
3.
Molecular sieve Y was modified by a combination of hydrothermal treatment,dealuminization with oxalic acid,and hydrothermal crystallization in the presence of the surfactant cetyl trimethyl ammonium bromide(CTAB).
采用水热、草酸脱铝及表面活性剂存在下的水热晶化相结合的组合法对Y型分子筛进行了改性,考察了表面活性剂十六烷基三甲基溴化铵(CTAB)存在下的CTAB加入量对Y型分子筛相对结晶度(Xc)、晶胞常数(a0)、硅铝比、比表面积、孔结构及加氢裂化性能的影响,并利用NH3-TPD对改性Y型分子筛进行了酸性表征。
5) hot water
热水
1.
Ultrastructural changes of gastric mucosa in chronic atrophic gastritis model caused by hot water in rats;
热水致大鼠萎缩性胃炎胃黏膜超微结构变化
2.
Temperature lowering technique of hot water with high temperature and pressure in Heibaishui ladder-shaped power station tunnel;
黑白水三级电站隧道高温高压热水降温技术
3.
Intelligent touchled application in the hot water serving system;
智能触摸屏在热水供应系统中的应用
6) Thermal water
热水
1.
Thermal waters in the shallow and deep reservoirs are of NaCl types both with the same B/Cl ratio.
羊八井地热田深、浅层热水都是Cl-Na类型,具有相同的B/Cl比值,说明深层热水在上升通道中与冷水相混合形成了浅层热水。
2.
In consideration of that karst fractures are developed, groundwater flows fast and there exists a strong aquifer with underground thermal water source, improved technique of combined grouting and freezing is used to plug water.
针对岩溶裂隙发育、地下水流速度快、且有地下热水源的强含水层的水文地质特征,采用改进的注浆、冻结联合堵水工艺,科学选用和配比注浆材料,实施立井井筒堵水加固,经检测,达到预期目的,为立井建井工作探索了新途径。
补充资料:晶体生长水热法
分子式:
CAS号:
性质: 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物,而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下,水的离子积很大;例如在600℃和202.65MPa时,水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质,在高温高压下可以溶于水。如果使体系产生一定的温度梯度,由于在不同温度下材料的溶解度不同,使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时,常在水中加入一定量的碱或酸,调节溶液的酸度,以调整材料在水中的溶解度。
CAS号:
性质: 在高温、高压水溶液中进行化学合成的一种方法。水热法不仅可以用于制备分子筛类的化合物,而且可以用来生长无机固体材料晶体。水的临界温度和压力分别为374℃和22MPa。在高温和高压下,水的离子积很大;例如在600℃和202.65MPa时,水的离子积是常温常压时的105倍。这意味着许多在通常条件下不溶于水的物质,在高温高压下可以溶于水。如果使体系产生一定的温度梯度,由于在不同温度下材料的溶解度不同,使材料晶体结晶出来。水热法生长晶体要在耐高压和高温的反应釜中进行。工业上应用水热法生长大尺寸的石英晶体。在生长晶体时,常在水中加入一定量的碱或酸,调节溶液的酸度,以调整材料在水中的溶解度。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。