1) 2024 alloy
2024合金
1.
The results show that the optimum parameters of 2024 alloy after T62 treatment are in following: solution temperature 498℃, solution time 30 min, storage period 12 h, ageing temperature 185℃, aging time 10 h.
结果表明,2024合金T62态的较优参数为:固溶温度498℃、固溶时间30min、放置时间12h、时效温度185℃、时效时间10h。
2) 2024 aluminum alloy
2024铝合金
1.
Effects of superplastic pre-treatment on the microstructure and properties of 2024 aluminum alloy;
超塑预处理对2024铝合金组织和性能的影响
2.
Effects of Air-slip Casting Parameters on the Microstructure of 2024 Aluminum Alloy;
气滑铸造工艺参数对2024铝合金微观组织的影响
3.
Effects of Aging on Mechanical Properties of 2024 Aluminum Alloy by Severe Cold Plastic Deformation;
时效制度对大冷变形2024铝合金力学性能的影响
3) 2024 T3 Al alloy
2024-T3Al合金
1.
Scanning microreference electrode technique (SMRE) was used to probe the potential imaging of 2024 T3 Al alloy in CeCl3 solution.
本文应用自行研制的扫描微参比电极技术(SMRE),原位测量经CeCl3溶液处理的2024-T3Al合金表面微区电位分布,并结合X光电子能谱(XPS)和交流阻抗谱(EIS),对Ce转化膜的成膜机理进行探讨。
4) aluminum alloy
2024铝合金
1.
The dynamic re crystallization of 2024 aluminum alloy during the extrusion process was studied by means of microanalyses.
通过显微分析,研究了2024铝合金挤压过程中的动态再结晶问题。
5) T3 aluminum alloy
2024-T3铝合金
1.
Features of electrochemical noise during pitting corrosion of 2024-T3 aluminum alloy in 3.0% Na_2SO_4 solution;
硫酸钠溶液中2024-T3铝合金孔蚀过程的电化学噪声特征
6) 2024/3003 aluminum alloy
2024/3003铝合金
1.
High temperature annealing of 2024/3003 aluminum alloy
2024/3003铝合金的高温退火研究