1) sand mould
砂型
1.
Based on the effect that Pb、As、Sn can increase the supercooling tendency of molten iron, it is possible to use the Pb、As、Sn containing pig iron produced in Fujian province of China and adopt sand mould casting process to obtain D-type graphite cast iron, and its production process was investigated.
基于Pb、As、Sn等元素有增大铁液过冷倾向的作用,利用含Pb、As、Sn的地方生铁,采用合金化和砂型铸造可以获得D型石墨铸铁,对其工艺方案进行了研究。
2.
The reason that sand mould quality and casting dimension precision by air impulsing are good in comparison with highpressure squeezing is expatiated.
用自行设计的砂型回弹测试仪,检测了高压压实与气冲紧实两种高紧实度砂型的回弹,运用型砂微变形理论和流变学理论,对测试结果进行对比分析,阐述了气冲造型比高压造型砂型质优而铸件尺寸精度高的原因。
3.
Based on the theory of green sand micro-deformation and the theory of rheorlogy,the test results were analyzed,and the mechanism of springback was proposed, and the main parameters influencing springback of high compacted sand moulds were discussed,which could be employed as a basis for selecting and evaluatin.
在湿型砂气冲紧实与慢压压实的过程中,用自行设计的砂型回弹测试仪,检测了砂型内应力与时间的动态关系曲线及高紧实度砂型的回弹,运用型砂微变形研究的理论基础和流变学理论,对测试结果进行分析,揭示了高紧实度型砂回弹的机理及影响回弹的主要因素,为型砂紧实工艺的选择与评价提供了依据。
2) sand mold
砂型
1.
The effect of different casting methods of sand mold and metal mold on the mechanical properties and fracture surfaces of ZL210A casting aluminum alloy of casting,solid-solution and aging was investigated.
采用砂型和金属型两种不同铸造方法对铸态、固溶态和时效态ZL210A合金性能及断口形貌的影响进行研究。
3) molding sand
型砂
1.
Study and Development on a Measuring System for High Temperature Behavior of Molding Sand;
型砂高温性能检测系统的研制
2.
DH-1 Type Automatic Measure & Control System for Moisture Content in Molding Sand;
DH-1型型砂水分自动测控系统
3.
Measuring and Controlling System of Moisture Ratio in Molding Sand Based on Two Level Closed Loop Control;
基于两级闭环控制的型砂水分在线测控系统
4) moulding sand
型砂
1.
Studies on the property of moulding sand binder of non-environmental pollution;
无公害型砂粘结剂性能研究
2.
The comprehensive properties analysis of moulding sand was showed withpractical examples, and some effective measures to intensify sand properties control was proposed in order toprevent works from economic loss caused by severe fluctuation of sand properties.
介绍了湿型砂性能和铸造缺陷之间的关系,分析了型砂性能对铸件质量的影响,以实例说明型砂综合性能分析。
3.
This paper analyses the technological process of moulding sand compounding,and con- trolled by PC,then yields good results.
本文分析了型砂配制的工艺,用 PC 对其进行了控制,获得了良好地控制效果。
5) green sand
型砂
1.
Quality automatic measurement and control techniques of green sand are always important study problems in the domain of foundry.
型砂质量的自动检测与控制一直是铸造领域的重要前沿研究课题之一。
2.
It is significant to investigate the stress-strain relationship of green sand to control the molding quality.
利用侧限压缩试验,研究了松散型砂在侧限应力状态下的力学行为,描述型砂压实状态的物理量,提出了型砂的瞬时压缩模量与压缩状态相关的假设。
3.
Property test and quality control of green sand are still important study problems in the domain of foundry.
分析了三种不同的型砂质量控制理念,评述了湿型粘土砂性能和组分的离线及在线自动检测技术和不同类型的型砂质量自动控制系统的研究与应用状况,特别介绍了近几年来国内外的研究成果及目前主要应用的砂处理系统,并从控制手段及控制思想上分析了型砂质量控制技术的发展趋势。
6) moulding sands
型砂
1.
The triaxial mechanics properties of a resin sand at elevated temperature are revealed through the recently developed trixaial apparatus for moulding sands.
利用新研制的型砂高温三轴测试手段，首次测定了常用树脂型砂在围压作用下的高温三轴力学性能。
补充资料：材料保护:砂型乾燥炉
砂型乾燥炉
对铸造用的砂型或型芯进行加热﹐使其所含水分汽化﹑蒸发以达到乾燥目的的工业炉。砂型或型芯中的有机物﹐如木屑等﹐也在加热过程中被烧去﹐从而使砂型的透气性增加。型芯中的一些黏接剂﹐如油类和沥青等﹐经过加热才具有黏接能力﹐从而使型芯的强度增加。
乾燥温度取决於砂型或型芯的物料组成﹐砂型的乾燥温度为400～500℃﹐型芯的乾燥温度为200～350℃。这种炉子多为火焰炉﹐要求炉内有良好的气流循环条件。炉室宽度大於2米时两侧应设火道﹐中间设排烟道(图1 双侧火道乾燥炉示意图 )。炉室宽度小於2米时可一侧设火道﹐另一侧设排烟道(图2 单侧火道乾燥炉示意图 )。砂型和型芯乾燥炉一般做成带有炉门的室状炉膛。砂型或型芯装在台车上﹐沿轨道送入炉内加热(乾燥)。砂型在炉内的乾燥时间﹐依装载量多少﹑砂型大小和物料组成情况而定。当砂型或型芯的品种同一﹑批量很大时﹐则採用连续式乾燥炉﹐用输送链条或活动小车将砂型或型芯连续地通过划分有温度区段的炉内进行乾燥﹐这种炉型的乾燥效率高。
随著红外线技术的发展﹐远红外乾燥炉已广泛应用。发射远红外线的器具有各种电热式远红外辐射器和煤气远红外辐射器。辐射器一般由远红外涂料层﹑发热体或热源﹑基体和附件组成。涂料层在一定温度下能发射出所需要的远红外线。远红外线的波长范围为6～15微米﹐具有很高的穿透能力﹐用於乾燥砂型时﹐水分蒸发能力大於用烟气乾燥﹐因而可以缩短乾燥週期。
对铸造用的砂型或型芯进行加热﹐使其所含水分汽化﹑蒸发以达到乾燥目的的工业炉。砂型或型芯中的有机物﹐如木屑等﹐也在加热过程中被烧去﹐从而使砂型的透气性增加。型芯中的一些黏接剂﹐如油类和沥青等﹐经过加热才具有黏接能力﹐从而使型芯的强度增加。
乾燥温度取决於砂型或型芯的物料组成﹐砂型的乾燥温度为400～500℃﹐型芯的乾燥温度为200～350℃。这种炉子多为火焰炉﹐要求炉内有良好的气流循环条件。炉室宽度大於2米时两侧应设火道﹐中间设排烟道(图1 双侧火道乾燥炉示意图 )。炉室宽度小於2米时可一侧设火道﹐另一侧设排烟道(图2 单侧火道乾燥炉示意图 )。砂型和型芯乾燥炉一般做成带有炉门的室状炉膛。砂型或型芯装在台车上﹐沿轨道送入炉内加热(乾燥)。砂型在炉内的乾燥时间﹐依装载量多少﹑砂型大小和物料组成情况而定。当砂型或型芯的品种同一﹑批量很大时﹐则採用连续式乾燥炉﹐用输送链条或活动小车将砂型或型芯连续地通过划分有温度区段的炉内进行乾燥﹐这种炉型的乾燥效率高。
随著红外线技术的发展﹐远红外乾燥炉已广泛应用。发射远红外线的器具有各种电热式远红外辐射器和煤气远红外辐射器。辐射器一般由远红外涂料层﹑发热体或热源﹑基体和附件组成。涂料层在一定温度下能发射出所需要的远红外线。远红外线的波长范围为6～15微米﹐具有很高的穿透能力﹐用於乾燥砂型时﹐水分蒸发能力大於用烟气乾燥﹐因而可以缩短乾燥週期。