1) Free formaldehyde content
游离甲醛含量
1.
The tea waste powder with different sizes as an additive was used to urea-formaldehyde (UF) resin, and the effects of the tea waste powder sizes and amount on the free formaldehyde content of UF resin, the formaldehyde emission, and bond strength of UF resin bonded plywood were studied in this paper.
将不同颗粒度的茶叶废料粉添加到脲醛树脂胶中,研究了茶叶废料的颗粒度、加入量等对脲醛树脂胶黏剂的游离甲醛含量、黏接胶合板的甲醛释放量及胶合强度的影响。
2.
The effects of different formaldehyde/urea molar ratio Uron resins and different using methods on reducing free formaldehyde content of UF resins and formaldehyde emission value of its bonded plywood were studied.
研究了Uron树脂及其使用方法对降低脲醛树脂胶粘剂游离甲醛含量及胶接胶合板甲醛释放量的作用与效果。
3.
This paper reviews the research development of low molar ratio urea-formaldehyde resin as a wood adhesive,including free formaldehyde content,formaldehyde emission of its bonded products,synthesis, and the curing characteristics of the adhesive.
从脲醛树脂胶粘剂的游离甲醛含量及其胶接制品的甲醛释放量,低摩尔比脲醛树脂的合成及不同固化体系下低摩尔比脲醛树脂的固化特性等方面,综述了近几年来低摩尔比脲醛树脂作为木材胶粘剂的研究进展。
2) free-formaldehyde content
游离甲醛含量
1.
Analysis of influence factors for determination of free-formaldehyde content inadhesives;
胶粘剂中游离甲醛含量检测的影响因素分析
2.
One adhesive was obtained with better shear strength,water-resistance and less free-formaldehyde content (<1%
从而获得一种高剪切强度、高耐水性、游离甲醛含量低于１％ 的胶料。
3) low free formaldehyde
低游离甲醛含量
4) content of free formaldehyde
游离甲醛释放量/含量
5) free formaldehyde emission
游离甲醛释放量
1.
88 mg/100 g free formaldehyde emission,meeting E, graded GB 18580-2001《Formaldehyde emission of interior decoration material-com.
用这种改性树脂压制的中密度纤维板(MDF)性能可达到国家标准优等品的要求,游离甲醛释放量也可达到国标GB 18580-2001《室内装饰装修材料-人造板及其制品中甲醛释放量》中E1级要求。
2.
The ammonia treatment could reduce the free formaldehyde emission of MDF, and the p.
采用氨气处理法降低MDF游离甲醛释放量的效果明显,可使板材的游离甲醛释放量控制在9mg/100 g以内,达到E1级级标准要求。
6) Formaldehyde emission
游离甲醛释放量
1.
Formaldehyde emission of the plywood can reach JAS F2 or F3 grade according to the species of poplar veneers respectively.
胶合板游离甲醛释放量视单板树种不同分别达到ＪＡＳ规定的Ｆ２级和Ｆ３级指标。
补充资料：《纺织品纤维含量的标识》(FZ／T01053—1998)
《纺织品纤维含量的标识》(FZ／T01053—1998)
Textiles-Designation of Fibre Content
FangZhiPin Xian明1 Honliong de BiaOZhi《纺织品纤维含t的标识》(万刀T 01053一1998)(爪荡￡幼郎.加匆刁以勿nof踢。。几饱瓜)纤维种类及其含量是纺织品品质标志的重要内容之一。根据纺织制品形式和结构，提出了标注纤维含t的具体要求，解决了不同产品标识的统一问题，如带里料的产品应对里和面分别标注;带填充物的产品应把填充物和套分别标注;二种以上的不同织物拼接或镶嵌的产品应分别标注不同织物;只起装饰作用而不作为产品主体的可以不标。规定统一采用国家标准规定的纤维名称，避免了任意标注商品名称、外来语名称等造成的纤维名称混乱问题;规定了以成品中某种纤维的量占纤维总量的百分数表示，而不以生产实际的投料比例标注，解决了纤维含t概念(即基数不清)的问题。明确规定了各种纺织品的纤维含量允差，既与原有的纺织品标准衔接，又明确了各种单一纤维纯纺、二组分或多组分纤维混纺或交织产品的明示含t值与实际值可允许的差值，使标准具有可操作性，解决了含t偏差判定的根本问题，使市场抽查有据可依。对统一纤维成分及其含量的标识起到了积极的指导作用，对保护消费者的利益，维护生产者的合法权益有着重要意义。(郑宇英)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条