1) pyrolysis temperature
裂解温度
1.
Effects of the pyrolysis temperature at the first cycle and Si content on the mechanical properties and anti-oxidation properties were investigated.
首先考察首周期裂解温度对2D Cf/SiC-Si材料力学性能的影响,结果表明,首周期采用1200℃裂解,所制备的2D Cf/SiC-Si复合材料界面结合较好,弯曲强度和断裂韧性分别达到305。
2.
The effects of the pyrolysis temperature on the microstructure and mechanical properties of 2D Cf/Si-O-C composites were investigated.
以二维碳纤维布、硅树脂先驱体、SiC微粉和乙醇溶剂为原料,采用先驱体转化工艺制备了2D Cf/Si-O-C复合材料,考察了裂解温度对材料结构和性能的影响。
3.
In this paper synthesis of polyferrocarbosilane(PFCS) was studied, synthesis techniques including reaction temperature, pyrolysis temperature and ferrocene were investigated.
本文研究了聚铁碳硅烷的合成,探索了裂解温度、反应温度、二茂铁等因素对合成聚铁碳硅烷(PFCS)工艺的影响;元素分析、红外光谱、氢谱分析表明:铁被引入到聚铁碳硅烷(PFCS)中,PFCS与聚碳硅烷(PCS)的结构相似。
2) pyrolytic temperature
裂解温度
1.
The temperature dependence of conductivity of polypyrrolone (PMDA DAB) film pyrolyzed at different pyrolytic temperatures was measured as a function of the applied pressure.
通过对裂解聚吡咙（ＰＭＤＡ－ＤＡＢ）薄膜导电性环境温度、裂解温度及压力关系的研究表明：其室温导电率随所加压力与裂解温度的升高而增加。
3) COT(coil outlet temperature)
裂解炉出口温度
4) Low-temperature pyrolysis
低温裂解
1.
The low-temperature pyrolysis process for oil production from sewage sludge is introduced.
对城市生活污水处理厂剩余活性污泥低温裂解过程进行了催化剂的筛选,筛选出了能使污泥最低裂解温度降低20℃且能提高油产量的催化剂CuSO4和Fe2O3。
5) pyrolysis
[英][pai'rɔlisis] [美][paɪ'rɑləsɪs]
高温裂解
1.
By pyrolysis of iron(Ⅱ)phthalocyanine(FeC32N8H16)at 800~1 000 ℃ under low pressure(Ar/H2),large-scale of vertically aligned car.
文章在低压条件下采用酞菁铁高温裂解法,在800～1000℃,以石英玻璃为基底,制备了大面积高度定向的碳纳米管。
2.
The preparation methods and properties of ultrafine,highly pure and mutli -phase SiC ceramic powders using sol -gel and through pyrolysis of organic matters by Laser,Plasma and CVD technique in later 1980s were emphatically described.
本文简要的介绍了碳化硅(SiC)原料制备技术的进展,着重描述八十年代后期运用Laser、Plasma、CVD等技术高温裂解有机物和Sol—Gel等方法制备超细、超纯、复相碳化硅陶瓷粉末的方法与性能,以期获得高性能的碳化硅结构陶瓷。
3.
PCB were pyrolysed at 750℃ and the pyrolysis products were analysed using GC-MS(FID),ICP-AES.
采用温控管式炉在750℃条件下,对废弃印刷线路板进行高温裂解,以分离回收其中的有机和金属材料。
6) reference temperature To
解理裂纹开始温度
1.
It was found the reference temperature To for 10Ni8CrMoV steel is very low and close to-151 ℃ considering the uncertainty for the testing results.
针对10Ni3CrMoV钢和10Ni8CrMoV钢进行了解理裂纹开始温度T0和夏比冲击韧脆转变温度TCVN的测定,并将两种试验结果进行了比较。
补充资料：裂解温度
分子式：
CAS号：
性质：石油烃分子在反应器中发生裂解生成较小分子的反应温度。裂解过程为强吸热反应，为获得良好的选择性，需在很短时间内供给反应所需热量来维持反应物短停留时间反应所需高温。供热可采用外热式(通过某种媒介将热量传递给反应物料，如金属管壁、热载体等)和内热式(通过部分原料燃烧发出的热量供另一部分原料裂解)两种方式。烃类裂解为非等温反应。在管式反应器中发生的裂解，反应温度随管长而升高，一般将物料在反应器中的最高温度(炉管出口温度)称为裂解温度。而在非管式炉中发生的裂解，反应温度往往随反应时间增长而下降，一般将反应区的物料最高温度或温度变化范围称为裂解温度。裂解温度根据裂解原料性质、反应器的类型和对产品的需求来确定。制取乙烯、丙烯产品的烃类裂解温度一般为760～900℃，以制乙炔为主的裂解温度一般为1000～1500℃。
CAS号：
性质：石油烃分子在反应器中发生裂解生成较小分子的反应温度。裂解过程为强吸热反应，为获得良好的选择性，需在很短时间内供给反应所需热量来维持反应物短停留时间反应所需高温。供热可采用外热式(通过某种媒介将热量传递给反应物料，如金属管壁、热载体等)和内热式(通过部分原料燃烧发出的热量供另一部分原料裂解)两种方式。烃类裂解为非等温反应。在管式反应器中发生的裂解，反应温度随管长而升高，一般将物料在反应器中的最高温度(炉管出口温度)称为裂解温度。而在非管式炉中发生的裂解，反应温度往往随反应时间增长而下降，一般将反应区的物料最高温度或温度变化范围称为裂解温度。裂解温度根据裂解原料性质、反应器的类型和对产品的需求来确定。制取乙烯、丙烯产品的烃类裂解温度一般为760～900℃，以制乙炔为主的裂解温度一般为1000～1500℃。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条