1) boric/sulfuric acid anodizing
硼酸-硫酸阳极化
1.
The effect of sulfuric acid,chromate acid and boric/sulfuric acid anodizing on fatigue performance of aeronautic aluminum alloys was studied by using S-N curve.
结果表明,对包铝的铝合金,不同阳极化试样的疲劳极限差别很小,对于铝合金基材,硫酸阳极化明显降低材料的疲劳极限,铬酸阳极化使材料的疲劳极限下降,而硼酸-硫酸阳极化不降低材料的疲劳极限。
2) sulfuric acid anodizing
硫酸阳极化
1.
Improvement of sulfuric acid anodizing process for aluminum and aluminum alloy;
铝及铝合金硫酸阳极化工艺的改进
4) 1-(2-pyridylazo)-2-naphthol(PAN)
硫酸阳极氧化液
1.
The color reaction conditions of Cu 2+ and 1-(2-pyridylazo)-2-naphthol(PAN)were researched,and a new method was developed for the determination of copper in sulfuric acid anodizing liquor.
研究了铜与1-(2-吡啶偶氮)-2-萘酚(PAN)的显色反应,建立了测定硫酸阳极氧化液中铜的新方法。
5) wide-temperature and fast-rate anodization of sulfuric acid anodizing
硫酸宽温快速阳极化
6) sulfuric acid-boric acid
硫酸-硼酸
1.
A mixed sulfuric acid-boric acid solution was used to prepare the anodized oxide film for Al alloys.
采用硫酸-硼酸混合液制备铝合金氧化膜。
补充资料：硫酸化焙烧
分子式：
CAS号：
性质：硫化矿物在氧化气氛中加热，部分脱硫转化为相应的金属硫酸盐的过程为硫酸化焙烧或部分脱硫焙烧。某些不含硫的精矿(如以轻稀土为主的氟碳铈矿-独居石混合精矿)与浓硫酸混合后在回转窑中连续高温(300～600℃)焙烧，使钍和稀土的磷酸盐和稀土的氟碳酸盐转化为钍和稀土的可溶性硫酸盐的过程，也是典型的硫酸化焙烧过程。
CAS号：
性质：硫化矿物在氧化气氛中加热，部分脱硫转化为相应的金属硫酸盐的过程为硫酸化焙烧或部分脱硫焙烧。某些不含硫的精矿(如以轻稀土为主的氟碳铈矿-独居石混合精矿)与浓硫酸混合后在回转窑中连续高温(300～600℃)焙烧，使钍和稀土的磷酸盐和稀土的氟碳酸盐转化为钍和稀土的可溶性硫酸盐的过程，也是典型的硫酸化焙烧过程。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条