1) acid-soluble aluminium
酸溶铝
1.
Spark source atomic emission spectrometric determination of acid-soluble aluminium and total aluminium in low alloy steel;
火花源原子发射光谱法测定低合金钢中酸溶铝和全铝
2.
Analysis of high content of acid-soluble aluminium in steel by spark source spectrometer;
用火花源发射光谱仪分析钢中高含量酸溶铝
3.
Since the CSP assembly line of Liangang on February,2004 putting formally into production,the control of acid-soluble aluminium in steel wasn't stable,and hitting ratio was low.
涟钢CSP生产线于2004年2月份正式投产以来,钢中酸溶铝的控制不稳定,酸溶铝命中率低。
2) acid-soluble aluminum
酸溶铝
1.
Study on the control of acid-soluble aluminum of high grade pipeline steel
高级别管线钢酸溶铝的控制
2.
The role of acid-soluble aluminum in aluminum-killed low carbon steel produced by TSCR is discussed.
对薄板坯连铸连轧低碳铝镇静钢中酸溶铝的作用进行了研究。
3.
Meanwhile,it analyses the acid-soluble aluminum in steel as well as desulfurised,nitrogen and oxygen in steel,and inclusions during the tapping process of BOF.
介绍了涟钢 CSP 生产线转炉出钢过程中高铝渣取代预熔渣调渣剂的试验情况,并针对试验过程钢中酸溶铝、转炉出钢过程脱硫及钢中氮氧、夹杂物的情况进行了分析,同时结合现场相关数据进行了热力学分析,结果表明,试验期间改质精炼渣的精炼效果并没有降低,经济效益上试验吨钢成本可降低1。
3) Soluble aluminum
酸溶铝
1.
The behavior of soluble aluminum in steel and its effect on steel properties are discussed.
就 Als问题经 1年的探索研究 ,并结合相关专家、学者的观点 ,探讨了酸溶铝对钢材性能的影响。
4) acid soluble aluminum
酸溶铝
1.
Mensuration of acid soluble aluminum contained in steel by means of emission spectrum PDA method;
应用发射光谱PDA法测定钢中酸溶铝的含量
5) dissolved aluminum
酸溶铝
1.
011 3 and dissolved aluminum must be in the range of 0.
结果表明:生产帘线钢时,为了得到塑性良好的夹杂物,钢液的氧活度应控制在0·0056~0·0113,而酸溶铝含量应控制在0·00010%~0·00025%范围内。
2.
The theoretical calculations and production data show that the content of SiO_2 in top slags and dissolved aluminum in molten steel were main factors on silicon content of molten steel for low carbon aluminum killed steel.
理论计算和实际生产数据表明,对于低碳、铝镇静钢,大包顶渣中SiO_2的浓度和钢水中的酸溶铝含量是控制钢水硅含量的主要因素。
6) acid-insoluble aluminium
酸不溶铝
1.
By the investigation and statistical analysis,it is found that acid-insoluble aluminium in steel is in the range of 0001%-0010%For carbon steel of aluminium content at 020%-050%,the subtraction of 005% from the content of total aluminium is defined as the content of acid-soluble aluminiumThe method is applied for guiding production of steel-smelting with satisfactory results
经过调查并统计发现,钢中酸不溶铝的质量分数在0 001%～0 010%之间。
补充资料：硫铝酸盐水泥和铁铝酸盐水泥
硫铝酸盐水泥和铁铝酸盐水泥
sulPhoaluminateCement and ferralUminate eement
硫铝酸盐水泥和铁铝酸盐水泥Sulphoaluminatecement and ferraluminate eement以石灰石、矾土(SAC为铝矾土，FAC为铁钒土)和石膏为原料制成的水泥。原料在回转窑中低温缎烧成以C4A3S、CZS和C6AF:(或C;AF)为主要矿物组成的熟料，通过掺入适量掺合料并共同粉磨而成水泥。为区别于硅酸盐水泥(第一系列)、铝酸盐水泥(第二系列)而将其称为第三系列水泥。 硫铝酸盐(S AC)水泥和铁铝酸盐(F AC)水泥由中国研制成功，并分别于1974年和1983年投入工业生产。目前生产的SAC类水泥品种有快硬、高强、膨胀、自应力和低碱硫铝酸盐水泥(GRC专用水泥);FAC类水泥品种有快硬、高强、膨胀和自应力铁铝酸盐水泥。 硫铝酸盐水泥和铁铝酸盐水泥具有以下特性:①较高的早期强度，而且具有不断增长的后期强度和满足使用要求的凝结时间，12小时至1天的抗压强度可达35一60 MPa，抗折强度达6.5一7.SMPa;其高强水泥3天抗压强度可达80一100 MPa，抗折强度达9.0一11.OMPa。②膨胀性能可在很大范围内调节。根据实际应用需要，其砂浆自由膨胀可在0.05一1.5%之间调节，其自应力值可在0.5一5.OMPa之间调节。③在0一10oC低温下使用，其早期强度(1一3天)是同标号硅酸盐水泥混凝土的5一10倍。在0一一20aC低温下使用，加入少量外加剂，3一7天的混凝土强度可达设计标号的70一80%。在正、负温交替条件下施工，对后期强度增长影响不大。实验室300次冻融循环，混凝土强度损失不明显。④水泥石结构较致密，其混凝土抗掺性是同标号硅酸盐水泥混凝土的2一3倍。⑤对海水、氯盐(NaCI，MgC12)、硫酸盐(NaZSO‘、MgSO‘、(NH‘)250小尤其是它们的复合盐类(MgSO‘+NaCI)，均具有很好的抗腐蚀性。其中铁铝酸盐水泥类更优于硫铝酸盐水泥类。⑥硫铝酸盐水泥类混凝土因早期(前3天)水化液相碱度较低，钢筋有轻微锈蚀。随时间的推移，水泥水化液相碱度提高，水泥石微结构致密，因此后期锈蚀情况无发展。而铁铝酸盐水泥由于水化液相碱度较高，对钢筋无锈蚀。 第三系列水泥适用于各种建筑工程，预应力混凝土构件和水泥制品。特别适用于地下工程、海港工程、抢修和抢建工程，制作自应力水泥压力管，高强管、桩和各种GRC制品。(苏慕珍)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条