1) chlorination-graft
氯化接枝
2) in-situ chlorinating graft
氯化原位接枝
1.
Synthesis of Modified CPVC by In-situ Chlorinating Graft Method;
氯化原位接枝技术制备改性CPVC的研究
2.
The graft copolymer of chlorinated PVC and maleic anhydride was synthesized via in-situ chlorinating graft copolymerization.
以氯化原位接枝法制备氯化聚氯乙烯接枝顺丁烯二酸酐的共聚物(CPVC-g-M AH),并用FT-IR、1H-NM R对产物进行表征;同时还讨论了反应温度、原料配比、反应时间以及膨润时间对产物接枝率的影响。
3.
A grafted copolymer(CPE-g-MMA),composed of poly(methyl methacrylate)(PMMA) as branched chains and chlorinated polyethylene(CPE) as backbone was synthesized by in-situ chlorinating graft copolymerization based on HDPE.
以聚乙烯(PE)为原料,采用氯化原位接枝方法合成以氯化聚乙烯(CPE)为骨架、聚甲基丙烯酸甲酯(PMMA)为支链的接枝共聚物(CPE-g-MMA)。
3) in-situ chlorinated graft
氯化原位接枝
1.
Styrene(St) modifying chlorinated polyvinyl chloride(PVC-C) was synthesized by in-situ chlorinated graft method.
采用氯化原位接枝技术制备了苯乙烯(St)改性氯化聚氯乙烯(PVCC)。
2.
The reaction process of PVC in-situ chlorinated graft method had been studied to graft some different monomers, in addition, the mechanical and rheological properties of graft polymer and blend of CPVC/LCPE (Low chlorinated polyethylene).
研究了不同单体通过氯化原位接枝改性方法，制备改性CPVC的反应过程；接枝物的力学性能、流变性能；CPVC与低氯含量氯化聚乙烯(LCPE)共混物的力学、流变性能。
4) chlorinated ABS grafting rubber powder
氯化ABS接枝胶粉
1.
The effects of category, dosage of chlorinated ABS grafting rubber powder, as well as the chlorine content on the properry of new ACS material were studied.
用气固相法制备氯化ABS接枝胶粉(氯化聚丁二烯),将产物与(苯乙烯/丙烯腈)共聚物(SAN)共混制得一种新型ACS材料。
5) graft CPE
接枝氯化聚乙烯
补充资料：氯乙烯与氯化聚乙烯接枝共聚物
分子式：
CAS号：
性质：氯化聚乙烯(CPE)之大分子链上进行氯乙烯接枝共聚后得到之产物。良好阻燃性、耐热、耐溶剂、耐冲击。以氯化聚乙烯分散于氯乙烯中进行悬浮接枝共聚制得。CPE含量为60％之产品用作PVC冲击改性剂。CPE含量为10％可直接用于加工成硬制品，如各种型材、管材。CPE含量为25％者可加入少量增塑剂，用于防水卷材、鞋料、密封条等软制品，增塑剂迁移性低。