1) Mooney scorch characteristic
门尼焦烧特性
2) Mooney scorch safety
门尼焦烧性能
1.
The scorch time t s and dynamic curing index Δ t during mixing in a wider range of temperatures (110～160 ℃) and rotor speeds (40～100 r·min -1 ) on Brabender torque rheometer and the Mooney scorch safety ( t 5 and Δ t 30 ) were measured by using CR mix prepared on an open mill.
测试了CR在较宽混炼温度 ( 110～ 160℃ )和转子转速 ( 4 0～ 10 0r·min- 1 )范围内的混炼焦烧时间ts 和动态硫化指数Δt以及相应温度范围的门尼焦烧性能 (t5和Δt30 ) ,指出门尼焦烧性能不能真正反映混炼胶在实际加工过程中的焦烧特性。
3) mooney scorch
门尼焦烧
4) Mooney scorch time
门尼焦烧时间
1.
The results showed that the test temperature had certain influence on the Mooney viscosity,Mooney scorch time and curing behavior of rubber compound;100 ℃ should have been chosen to determine the Mooney viscosity;120 ℃ or 130 ℃ for SBR should have been chosen to determine the Mooney scorch time in order to shorten the test time;185 ℃ should have been chosen to determine the curing behavior;t.
结果表明 ,试验温度对胶料的门尼粘度、门尼焦烧时间和硫化特性均有一定影响。
5) mixing scorch safety
混炼焦烧特性
1.
The mixing scorch safety ( t s and Δ t ) of four kinds of rubber compounds (NR,SBR,BR and NBR) was measured using a Brabender torque rheometer in a wide temperature range (100～140 ℃) and rotor speed range (20～80 rpm),and compared to Mooney scorch safety ( t 5 and Δ t 30 ).
采用Brabender转矩流变仪 ,在混炼温度为 10 0～ 14 0℃和混炼转子转速为 2 0～ 80r·min- 1 的条件下测试了4个胶种 (NR ,SBR ,BR和NBR)的混炼焦烧特性 (ts 和Δt) ,并与门尼焦烧特性 (t5和Δt30 )进行比较 ,指出门尼焦烧不能真正地反映混炼胶在实际加工过程中的焦烧特性。
补充资料：门尼焦烧
分子式：
CAS号：
性质：用门尼黏度计测得的混炼胶初期硫化特性的度量，通常由门尼黏度值-时间曲线上门尼值上升5个门尼值（用大转子）或3个门尼值（用小转）时所需时间来表示。门尼焦烧时间长短反映了胶料加工安全性能的好坏，在实际生产中应从保证胶料加工安全性和提高生产效率两个方面综合考虑，选定合适的门尼焦烧时间。
CAS号：
性质：用门尼黏度计测得的混炼胶初期硫化特性的度量，通常由门尼黏度值-时间曲线上门尼值上升5个门尼值（用大转子）或3个门尼值（用小转）时所需时间来表示。门尼焦烧时间长短反映了胶料加工安全性能的好坏，在实际生产中应从保证胶料加工安全性和提高生产效率两个方面综合考虑，选定合适的门尼焦烧时间。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条