1) peeling strength
剥离强度
1.
Several methods of improving peeling strength of polyurethane adhesive for shoes;
提高鞋用聚氨酯胶粘剂剥离强度的几种途径
2.
Analysis of the influence factors on peeling strength of the nonwonvens used for micro-fiber synthetic leather
浅析影响超纤合成革用非织造布剥离强度的因素
3.
The results showed that when ACM was added,the adhesive property of IIR to metal was greatly increased,and it could make 180° peeling strength enforcing 2～3 times due to synergestic effects of physical adhesion and chemical adhesion in the interface of blends-metal.
对剥离强度、断面形貌及表面能等的研究结果表明,引入ACM有效地改善了IIR与钢片的粘接性能,使其剥离强度提高2~3倍;并用ACM后,体系剥离强度的提高是物理黏着和化学黏着共同作用的结果;钢片-橡胶复合制件的破坏形式主要是橡胶部分的破坏及橡胶与胶黏剂之间的破坏。
2) peel strength
剥离强度
1.
Effect of crosslinking on T- peel strength of aqueous polyester polyurethanes;
聚酯型水性聚氨酯的交联对T剥离强度的影响
2.
Through the research of properties of peel strength,uptake water and glass-transition temperature ,the optimum method in disposing adhesive joints were obtained.
采用不同的表面处理方法处理粘接接头,在湿热老化条件下通过元素分析法测定了样品中碳、硅、氧的含量,以及对胶粘剂粘接接头剥离强度、吸水率,玻璃化温度等湿热老化性能进行了考查,得出最佳处理粘接接头的方法。
3.
The experiment data showed that the peel strength of adhesion for polyurethane elastomer and metals has the highest value 31 kN/m.
实验数据表明,聚氨酯弹性体硬度较高时,柔性材料与金属粘接的剥离强度最高可达31 kN/m,聚酯型聚氨酯弹性体与金属粘接比聚醚型聚氨酯弹性体的粘接性能好。
3) T-style peel strength
T剥离强度
1.
The effects of the content of carboxyl(COOH%),the mol ratio of-NCO and-OH(R Value),and the content of crosslinker on the properties of aqueous Polyurethane(PU) and T-style peel strength were discussed,and thus a kind of modified inner crosslinking aqueous polyurethane adhesive was synthesized.
通过改变羧基含量(COOH%)、异氰酸酯基(-NCO)与羟基(-OH)的摩尔比(R值)、交联剂用量,考察了它们对聚氨酯乳液的粘度、胶膜的耐水性及复合薄膜T剥离强度的影响,合成了一种内交联型复合薄膜用水性聚氨酯胶粘剂。
2.
It was found that T-Style peel strength dropped when content of butyl acrylate increased.
以PUA乳液作为复合薄膜胶粘剂时，发现随着BA含量的增加，复合薄膜的T剥离强度明显降低。
4) peel resistance strength
抗剥离强度
1.
The influences of copper ion content,sulfuric acid content and current density on the surface quality and peel resistance strength of the wrought rolled copper foil during roughening and curing treatment were discussed.
讨论了粗化处理及固化处理过程中铜离子含量、硫酸含量及电流密度等因素对压延铜箔表面质量及抗剥离强度的影响。
5) peeling strength tester
剥离强度仪
6) 180° peel strength
180°剥离强度
1.
The influence of sample width,times of press,time of sample placement,and roller speed to 180° peel strength of BOPP PSA were studied by orthogonal experiment.
通过正交试验,分析研究试样宽度、压辊的滚压次数、试样放置时间和压辊速度对180°剥离强度的影响。
补充资料：剥离强度
分子式：
CAS号：
性质：在贴合的制品上，沿纵向(或横向)切出长条作为试片。预先将一端剥离，分别由拉力机的上下夹具夹持，以一定分离速度将整个试片分离，记录其最大的负荷值，除以试样宽度，即为剥离强度。此法亦可检验胶黏带的黏牢度，有一个专门的试验方法称斯柯奇胶带试验方法，对测定条件做了专门的规定。剥离强度的单位是N/m。剥离试验只有对软的片材或薄膜做检验。
CAS号：
性质：在贴合的制品上，沿纵向(或横向)切出长条作为试片。预先将一端剥离，分别由拉力机的上下夹具夹持，以一定分离速度将整个试片分离，记录其最大的负荷值，除以试样宽度，即为剥离强度。此法亦可检验胶黏带的黏牢度，有一个专门的试验方法称斯柯奇胶带试验方法，对测定条件做了专门的规定。剥离强度的单位是N/m。剥离试验只有对软的片材或薄膜做检验。