1) potassium niobate
铌酸钾
1.
Research on the preparation process of potassium niobate powder by hydrothermal method;
铌酸钾粉体水热法制备的工艺研究
2) Potassium lithium niobate
铌酸钾锂
1.
Potassium lithium niobate (KLN) has good photoelectric,piezoelectric and nonlinear optical properties,which has broad application in integrated optics and integrated circuits.
铌酸钾锂具有良好的光电、压电及非线性光学性能,在集成光学、集成电路等领域具有广阔的应用前景。
2.
Raman spectra of a batch of potassium lithium niobate(KLN) crystals with different compositions were investigated.
测量了一批不同组分的铌酸钾锂晶体Ram an光谱,发现晶体中位于C格位的L i离子浓度对晶体Ram an光谱产生了强烈的影响:低L i含量晶体中[NbO6]7-八面体所对应的3个Ram an特征光谱线没有发生峰分裂,在100~400 cm-1范围出现的小峰与C格位L i离子浓度相关;当晶体中L i离子浓度增加时,与ν5所对应的Ram an峰在散射几何为X(ZY)Z对应的光谱中加宽,ν2振动模式在两种散射几何中均出现分裂峰,并在100~400 cm-1范围出现小峰数量增多;当L i离子浓度接近晶体化学组分时,微扰进一步加强,5ν所对应峰分裂成3个峰,ν1和ν2振动模式发生部分分裂,在100~400 cm-1范围小峰更为突出。
3.
A series of potassium lithium niobate (KLN) crystals with large size and good homogeity for composional ions have been grown.
用电阻加热提拉法生长了一系列较大尺寸 ,组分离子均匀性较好的铌酸钾锂晶体。
3) sodium potassium niobate
铌酸钾钠
1.
Based on the current research on lead-free piezoelectric ceramics,this work investigates the preparation and properties of Li-and Ta-doped sodium potassium niobate(LNKNT) ceramics.
文中在目前无铅压电陶瓷研究的基础上,进行了Ta、Li固溶改性铌酸钾钠无铅压电陶瓷(LNKNT)的制备和性质的研究。
5) potassium niobate (KNbO3)
铌酸钾(KnbO_3)
6) KSr_2Nb_3O_(10)
铌酸钾锶
补充资料：铌酸钾
分子式：KNbO3
CAS号：
性质：正交晶系，畸变钛钙矿型结构，点群C2V-mm2，晶格常数a=0.5698mm,b=0.5720mm,c=0.3971mm。密度4.62g/cm3，熔点1045℃，莫氏硬度4.5。为铁电晶体，居里点435℃，非线性系数d31=17.2×10-12m/V，相位匹配温度71℃（1.06μm），折射率na=2.2200，nb=2.5740,nc=2.1196(λ=1.06μm),自发极化强度0.32C/m2。以氧化铌和碳酸钾为原料，用凯泡罗斯法生长晶体。主要用于激光倍频、电光调制和光折变材料。
CAS号：
性质：正交晶系，畸变钛钙矿型结构，点群C2V-mm2，晶格常数a=0.5698mm,b=0.5720mm,c=0.3971mm。密度4.62g/cm3，熔点1045℃，莫氏硬度4.5。为铁电晶体，居里点435℃，非线性系数d31=17.2×10-12m/V，相位匹配温度71℃（1.06μm），折射率na=2.2200，nb=2.5740,nc=2.1196(λ=1.06μm),自发极化强度0.32C/m2。以氧化铌和碳酸钾为原料，用凯泡罗斯法生长晶体。主要用于激光倍频、电光调制和光折变材料。