1) EVOH-SO3K
聚乙烯-乙烯醇磺酸钾
2) potassium polyvinyl sulfate
聚乙烯醇硫酸钾
1.
Preparation of potassium polyvinyl sulfate by polymer reaction;
高分子反应制备聚乙烯醇硫酸钾
3) potassium polyvinylsulfate
聚乙烯醇硫酸酯钾盐
4) complex of PANI/PSSA-PVA
聚苯胺/聚苯乙烯磺酸-聚乙烯醇复合物
5) EVOH-SO_3Na
乙烯-乙烯醇磺酸钠
6) polystyrene sulfonic acid
聚苯乙烯磺酸
1.
In the aqueous phase,choosing polystyrene sulfonic acid as template doping agent,polyvinyl alcohol as film-forming agent,and aniline as monomer,and utilizing ammonium persulfate to initiate and synthesize the complex solid of PANI/PSSA-PVA,and it's aqueous solution,and then with the method of spin-coating,the corresponding complex electrochromic films is prepared.
在水相中,以聚苯乙烯磺酸(PSSA)为模板掺杂剂,聚乙烯醇(PVA)为成膜助剂,苯胺(An)为单体,过硫酸铵(APS)引发合成水溶性导电聚苯胺/聚苯乙烯磺酸-聚乙烯醇(PANI/PSSA-PVA)复合物固体及其复合溶液,用旋涂法制备了相应的复合电致变色膜。
2.
Water soluble conductive polyaniline (PAn) was synthesized by the oxidation of aniline(An) doped with ammonium persulfate(APS) and polystyrene sulfonic acid(PSSA) through the method of emulsion polymerization.
以苯胺(An)为单体,过硫酸铵(APS)为引发剂,采用现场乳液聚合法合成了可完全溶于水的聚苯乙烯磺酸(PSSA)掺杂聚苯胺(PAn)。
补充资料：聚乙烯醇缩乙醛
聚乙烯醇缩乙醛是由醋酸乙烯以甲醇或乙醇为介质，在过氧化苯甲酰存在下先反应生成聚醋酸乙烯酯，再于甲醇和硫酸存在下水解．加乙醛进行缩醛化、中和、沉淀、过滤、干燥而制得。略带微黄色的颗粒，无臭、无味。相对密度1．35，马丁耐热100 ℃．伸长率5％-10％，吸水性(24h／20℃)1.2%。溶于乙醇、丙酮、甲乙酮、环己酮、醋酸乙酯、二氯乙烷、苯、甲苯等。与酚醛树脂、硝酸纤维素、天然树脂等混溶。对金属、木材、皮革等有很强的粘接能力。