1) bimetallic powders
双金属粉
1.
Preparation of core-shell Cu-Ag bimetallic powders via electroless plating
化学镀法制备核壳型银-铜双金属粉
2.
Cu-Ag bimetallic powders whose grain size was similar to the copper powders,were prepared by reduction reaction with hydrazine as the reducing agent by means of inhibiting substitution reaction.
反应体系中引入强还原剂水合肼,通过反应条件的控制抑制置换反应,使银氨溶液优先发生液相还原反应,制备了与原铜粉粒径和形貌大致相同的铜-银双金属粉;采用XRD、EDX、激光粒度分析仪等检测方法对包覆双金属粉的晶相组成及含量、表面包覆层相组成及含量以及粒径分布等加以研究。
3) Ni-Ag bimetallic powder
镍-银双金属粉
1.
The micro Ni-Ag bimetallic powder with high temperature antioxygenic property was prepared by an electroless deposition technique.
采用化学镀法在镍粉表面包覆一层金属银,然后将这种包覆粉进行真空热处理,即可制得具有抗氧化作用的微米级镍-银双金属粉末。
4) Cu-Ag bimetallic powder
铜银双金属粉
1.
The Cu-Ag bimetallic powder prepared with substitutional reaction method has antioxidation behavior at the room temperature.
采用置换反应法制备铜银双金属粉,使用EDTA代替氨水作Ag+的络合剂,并螯合分散Cu2+,一次性制备了具有常温抗氧化性能的铜银双金属粉。
5) Cu-Ag bimetallic powder
铜-银双金属粉
1.
Research advance of preparing Cu-Ag bimetallic powder;
化学镀法制备铜-银双金属粉的研究进展
补充资料：双金属、多金属重整
分子式：
CAS号：
性质：采用含有两种或两种以上金属组元重整催化剂的催化重整过程。但反应器可以是固定床也可以是移动床。一般的双金属多指铂和铼，还有铂和锡、铂和铑等；多金属有铂、铼、钛或铂、铱再加上其他金属，这类催化剂活性好可以在较低压力下操作，如铂铼为1.4～1.8MPa，多金属催化剂在移动床甚至可低于0.7MPa。且芳烃转化率高，双金属固定床可达芳潜的120％，而移动床连续重整可达150％～170％。但双金属和多金属催化剂比单铂催化剂对原料中的杂质更敏感。
CAS号：
性质：采用含有两种或两种以上金属组元重整催化剂的催化重整过程。但反应器可以是固定床也可以是移动床。一般的双金属多指铂和铼，还有铂和锡、铂和铑等；多金属有铂、铼、钛或铂、铱再加上其他金属，这类催化剂活性好可以在较低压力下操作，如铂铼为1.4～1.8MPa，多金属催化剂在移动床甚至可低于0.7MPa。且芳烃转化率高，双金属固定床可达芳潜的120％，而移动床连续重整可达150％～170％。但双金属和多金属催化剂比单铂催化剂对原料中的杂质更敏感。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条