1) surface resistivity
表面电阻率
1.
The in-situ measurement of surface resistivity of thermal control coatings;
热控涂层表面电阻率原位测量方法研究
2.
A quaternary ammonium salt compound with a long chain of 12 carbon atoms was synthesized and used as an antistatic agent to be added into plasticized poly(vinyl chloride) (PVC), and the structure and properties of such PVC materials were studied by surface resistivity, mechanical property and scanning electronic microscope tests.
结果表明:随合成长链季铵盐的添加量增大,PVC材料的表面电阻率降低,较小的添加量(4。
3.
The effect of antistatic agent content,mixing time and moisture of atmosphere on the surface resistivity of PP were studied.
采用非离子型抗复合抗静电剂通过共混复合的方法制备出具有抗静电性能的聚丙烯,考察了抗静电剂的添加量、放置时间、环境湿度对抗静电聚丙烯的表面电阻率的影响。
2) surface resistance
表面电阻率
1.
The results by the preparation of the complex membrane with antistatic property were that the surface resistance rate of the complex membrane was 108Ω/cm when SiO_2 wrapped na.
改性纳米SiO2/聚丙烯酸酯复合膜制备与性能研究表明当纳米SiO2与聚丙烯酸酯树脂质量分数22%时,复合膜的表面电阻率可达到108Ω/cm,复合膜为半透明膜;复合膜表面具有一定的亲水性,烘干后,放在20～30℃、湿度60%～80%的空气中2～4h后,复合膜表面电阻率降低到106Ω/cm。
3) surface resistivity
表面电阻率，表面电阻系数
4) Surface Resistance
表面电阻
1.
Strain effect on microwave surface resistance of YBa_2Cu_3O_(7-δ)/LaAlO_3 and Tl_2Ba_2CaCu_2O_8/LaAlO_3 high temperature superconducting thin films;
YBa_2Cu_3O_(7-δ)/LaAlO_3和Tl_2Ba_2CaCu_2O_8/LaAlO_3高温超导薄膜内的应变对其微波表面电阻影响的研究
2.
The surface resistance Rs was measured by the four-probe method described in ASTM F 390.
分别用四探针法(ASTM F390)和双轴传输线法(ASTM D 4935-99)测量导电涤纶织物的表面电阻和电磁屏蔽效能。
3.
The results showed that the material with 5% content of carbon black could meet the requirement of the performance of motor blower fan material as the surface resistance reaching 1×108Ω.
结果表明,炭黑的质量分数为5%时,材料表面电阻率为108Ω数量级,力学性能优良,达到电机用塑料风叶材料的指标要求,并可应用于其它对抗静电性能要求较高的场合,用于制造某些结构件。
5) Surface resistivity
表面电阻
1.
Antistatic properties of carbon black (CB) filled plasticized poly(vinyl chloride) (PVC) were studied using surface resistivity tester and SEM.
采用表面电阻测试和扫描电镜 ,分析研究了软质聚氯乙烯 (PVC)树脂与炭黑 (CB)复合体系的抗静电性与炭黑含量、分布形态、PVC树脂型号及混炼塑化工艺之间的关系。
2.
When nonionic electrostatic resistant is mixed with assistant electrostatic resistant,the composite's surface resistivity will be reduced to 3×10 8Ω or below.
实验结果表明 ,八溴联苯醚与 Sb2 O3 互配体系的氧指数可达 2 7以上 ;非离子型抗静电剂配以辅助抗静电剂 ,可使材料的表面电阻降至 3× 1 0 8Ω 以
3.
In fact,the surface resistivity of these composites is analyzed.
研究复合材料的热性能、微观结构、表面电阻和结晶行为,结果都表明OMMT对PA66有明显的影响。
6) frequency selective surface with resistance patch
电阻贴片频率选择表面
1.
Absorbing performance of frequency selective surface with resistance patch;
电阻贴片频率选择表面(FSSR)的吸波性能研究
补充资料：表面电阻率
分子式：
CAS号：
性质：又称比表面电阻。在数值上等于两平行电极各1cm长，相距1cm时的表面电阻。表征电介质材料表面绝缘性能的重要指标。表达式为表面电阻率(式中Rs为测量时电阻；b为电极长；l是两平行电极的距离)，单位为Ω。
CAS号：
性质：又称比表面电阻。在数值上等于两平行电极各1cm长，相距1cm时的表面电阻。表征电介质材料表面绝缘性能的重要指标。表达式为表面电阻率(式中Rs为测量时电阻；b为电极长；l是两平行电极的距离)，单位为Ω。