1) Zone melting
区域熔炼
1.
high purity indium was prepared by the method of a combination of electrolytic refining and zone melting.
采用电解精炼 区域熔炼法 ,获得了 99 9999%高纯铟。
2.
The methods of preparing high purity iron include solvent extraction,ion exchange,electrolytic refining,zone melting,and so on.
本文介绍了溶剂萃取、离子交换、电解精炼和区域熔炼等冶金提纯方法在高纯铁制备过程中的应用。
2) zone-melting
区域熔炼
1.
The zone-melting temperature of YBaCuO tapes were decreased under 945□ by doping Ag and PbO in YBaCuO films, which made zone-melting process possible with Ag substrate not melted.
通过掺杂Ag和PbO的方法降低YBaCuO的区熔温度到945℃以下,从而能够在金属Ag基底上进行区域熔炼,获得有织构的超导带材。
3) Regional Smelt
区域熔炼
1.
Making the Metal in High Solidification by the Way of Regional Smelt;
区域熔炼法制备高纯度金属
2.
Method of regional smelt has been adopted in the electronic industrial production.
在电子工业生产中采用区域熔炼的方法，能将金属的纯度提高到99。
4) zone refining
区域熔炼法
1.
The three main methods for high purity zinc preparation,including electrolytic method,vacuum distillation,zone refining,are summarized and compared in this paper.
本文对目前高纯锌的三种主要制备方法(电解法、真空蒸馏法、区域熔炼法)进行了综述和比较。
5) zone melting
区域熔融[炼]
6) zone-melting
区域熔炼<冶>
补充资料：区域熔炼
指根据液体混合物在冷凝结晶过程中组分重新分布（称为偏析）的原理，通过多次熔融和凝固，制备高纯度的（可达99.999％）金属、半导体材料和有机化合物的一种提纯方法，属于热质传递过程。此法是由W.G.范在1952年提出的，最初应用于高纯度锗的生产。
区域熔炼的典型方法是将被提纯的材料制成长度为0.5～3m（或更长些）的细棒，通过高频感应加热,使一小段固体熔融成液态，熔融区液相温度仅比固体材料的熔点高几度，稍加冷却就会析出固相。熔融区沿轴向缓慢移动（每小时几至十几厘米）。杂质的存在一般会降低纯物质的熔点，所以熔融区内含有杂质的部分较难凝固，而纯度较高的部分较易凝固，因而析出固相的纯度高于液相。随着熔融区向前移动，杂质也随着移动，最后富集于棒的一端，予以切除。一次区域熔炼往往不能满足所要求的纯度，通常须经多次重复操作，或在一次操作中沿细棒的长度依次形成几个熔融区。
区域熔炼设备简单，产品纯度高，操作可以自动化，但生产效率低。目前，已经用于制备铝、镓、锑、铜、铁、银等高纯金属材料。
区域熔炼的典型方法是将被提纯的材料制成长度为0.5～3m（或更长些）的细棒，通过高频感应加热,使一小段固体熔融成液态，熔融区液相温度仅比固体材料的熔点高几度，稍加冷却就会析出固相。熔融区沿轴向缓慢移动（每小时几至十几厘米）。杂质的存在一般会降低纯物质的熔点，所以熔融区内含有杂质的部分较难凝固，而纯度较高的部分较易凝固，因而析出固相的纯度高于液相。随着熔融区向前移动，杂质也随着移动，最后富集于棒的一端，予以切除。一次区域熔炼往往不能满足所要求的纯度，通常须经多次重复操作，或在一次操作中沿细棒的长度依次形成几个熔融区。
区域熔炼设备简单，产品纯度高，操作可以自动化，但生产效率低。目前，已经用于制备铝、镓、锑、铜、铁、银等高纯金属材料。