1) polymeric sponge
有机泡沫
1.
Fabrication of porous ceramics using polymeric sponge dipping method;
有机泡沫浸渍法制备多孔陶瓷
2.
The open cell alumina foam ceramics were prepared by impregnating a polymeric sponge with aqueous ceramic slurry.
采用有机泡沫前驱体浸渍工艺制备氧化铝泡沫陶瓷。
3.
The powder of Al_2O_3 were added wollastonite or cordierite, adopted polymeric sponge dipping in slurry, produced by sintering of porous ceramics, and strives to achieve optimum process parameters.
即以Al_2O_3为基体粉料，分别添加硅灰石或堇青石，利用有机泡沫浸渍法成型，通过烧结制备出多孔陶瓷，并力求获得最佳工艺参数。
2) organic foam small-sphere
有机泡沫微球
3) organic foam material
有机泡沫材料
4) organic foam impregnation
有机泡沫浸渍法
1.
Then the powders were mixed with Al2O3-MgO -H3PO4 binder to prepare slurry, and the porous calcium phosphate bioceramic scaffold for bone tissue engineering was fabricated by organic foam impregnation.
本研究利用直接沉淀法和两步中和法合成磷酸钙粉体,并以其为原料, Al2O3-MgO-H3PO4为粘结剂配制浆料,采用有机泡沫浸渍法制备了骨组织工程磷酸钙生物陶瓷多孔支架。
6) silicone foam plastics
有机硅泡沫塑料
补充资料：有机硅泡沫塑料
分子式：
CAS号：
性质：亦即聚甲基苯基硅氧烷泡沫塑料(polymethyl-phenyl siloxane foam)。有机硅泡沫塑料商品分两类，一类是由硅树脂、填料、发泡剂和催化剂组成的粉状料，压缩强度1.94MPa(20℃)，0.58MPa(250℃)，0.54MPa(300℃)；线收缩率为0.5%(250℃/lOOh)，2.0%(300℃/100h)；相对介电常数2.1(1010Hz)；介质损耗因数0.013(1010Hz)；200℃热导率8.72×10-2W/(m·K)，20～200℃线膨胀系数(7.7～10) ×10-5℃-1由无溶剂硅树、填料、发泡剂和催化剂经熔融混合后粉碎而制取。当加热到160℃，发泡剂分解，同时树脂交联固化成泡沫塑料。另一类是由含硅羟基和硅氢键的两种液体聚硅氧烷混合，加入催化剂后，利用反应放出的氢气使之发泡并交联得到泡沫体。有机硅泡沫塑料质轻、耐高温、抗湿，可作为宇航器、火箭中的填充材料及高温绝热体。
CAS号：
性质：亦即聚甲基苯基硅氧烷泡沫塑料(polymethyl-phenyl siloxane foam)。有机硅泡沫塑料商品分两类，一类是由硅树脂、填料、发泡剂和催化剂组成的粉状料，压缩强度1.94MPa(20℃)，0.58MPa(250℃)，0.54MPa(300℃)；线收缩率为0.5%(250℃/lOOh)，2.0%(300℃/100h)；相对介电常数2.1(1010Hz)；介质损耗因数0.013(1010Hz)；200℃热导率8.72×10-2W/(m·K)，20～200℃线膨胀系数(7.7～10) ×10-5℃-1由无溶剂硅树、填料、发泡剂和催化剂经熔融混合后粉碎而制取。当加热到160℃，发泡剂分解，同时树脂交联固化成泡沫塑料。另一类是由含硅羟基和硅氢键的两种液体聚硅氧烷混合，加入催化剂后，利用反应放出的氢气使之发泡并交联得到泡沫体。有机硅泡沫塑料质轻、耐高温、抗湿，可作为宇航器、火箭中的填充材料及高温绝热体。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。