1) fuscous ceramic film
深色陶瓷膜
1.
Meanwhile X-ray Energy Spectrometer(XES) was used to examine and analyse the composition of the fuscous ceramic films.
通过正交实验在AZ91镁合金表面制备出了深色陶瓷膜,并进一步研究了陶瓷膜的耐蚀性。
2) black ceramic coating
黑色陶瓷膜
1.
Effects of electrolyte parameters on black ceramic coatings prepared by micro-arc oxidation of aluminum alloy;
电解液参数对铝合金微弧氧化黑色陶瓷膜性能的影响
2.
Influences of main parameters such as composition of electrolyte and electrical parameters in preparing black ceramic coating by microplasma oxidation on ADC12 aluminum alloy were studied.
研究了ADC12铝合金表面微等离子体氧化法制备黑色陶瓷膜的电解液成分和电参数等对膜层性能的影响。
3) ceramic film colourity
陶瓷膜色度
1.
The effect of processing parameters on ceramic film colourity is studied.
通过正交试验获得适合于镁合金表面微弧氧化深色陶瓷膜处理的新型溶液配方,进而研究了不同工艺参数对陶瓷膜色度的影响;利用XES,XPS对陶瓷膜成分、结构进行分析,探讨了不同色度陶瓷膜层显色机理。
4) green ceramic coating
绿色陶瓷膜
1.
It was found that uniform and dense green ceramic coating could be prepared from the electrolyte containing 10 g/L NaAlO2,1 g/L K2Cr2O7,and a small amount of NaOH and H2O2,via micro-arc oxidation coloring .
为了开发更多颜色的微弧氧化陶瓷膜层,通过试验在AZ91D镁合金表面制备出了绿色陶瓷膜层,分别研究了着色盐K2Cr2O7添加量为0。
5) yellow ceramic coating
黄色陶瓷膜
1.
Moreover,the yellow ceramic coating stably retained its color and had an in-creased corrosion potential than that of the Al alloy substrate,showing that the coating had better corrosion resistance than the bare Al alloy.
结果表明:陶瓷膜层致密,与基体结合紧密;膜层主要组成相为Al,Al2O3,Mn5O8,Mn3O4,MnWO4;黄色陶瓷膜色泽稳定,较铝合金基体腐蚀电位有所提高。
6) Black ceramic oxide-film
黑色陶瓷氧化膜
补充资料：多孔陶瓷支撑体膜
分子式：
CAS号：
性质：在多孔陶瓷体上附着的微孔陶瓷膜层。膜层厚度一般在几微米到几十微米，外径孔径一般为0.1～0.5μm，个别也有厚度达3～5μm、孔径10μm的。多采用氧化铝、二氧化钛和二氧化锆等作膜材料。制法是：用电机带动陶瓷支撑体旋转，当溶胶液(膜材料)滴落在支撑体上，就会迅速地敷覆到支撑体表面，待溶剂蒸发、凝胶化和干燥成膜后，经热处理而制成氧化物薄膜。现已为食品(含饮料)、医药、生物技术和环境保护等领域开发利用。
CAS号：
性质：在多孔陶瓷体上附着的微孔陶瓷膜层。膜层厚度一般在几微米到几十微米，外径孔径一般为0.1～0.5μm，个别也有厚度达3～5μm、孔径10μm的。多采用氧化铝、二氧化钛和二氧化锆等作膜材料。制法是：用电机带动陶瓷支撑体旋转，当溶胶液(膜材料)滴落在支撑体上，就会迅速地敷覆到支撑体表面，待溶剂蒸发、凝胶化和干燥成膜后，经热处理而制成氧化物薄膜。现已为食品(含饮料)、医药、生物技术和环境保护等领域开发利用。