1) cement-based
水泥基
1.
Experimental study on cement-based non-shrinkage composite grouting material;
水泥基无收缩复合灌浆料的实验研究
2.
Study on microwave-absorbing properties of carbon-fiber-reinforced cement-based composites;
碳纤维增强水泥基复合材料的吸波性能研究
3.
Application of cement-based osmotic crystallization damp-proof;
水泥基渗透结晶型防水做法的应用
2) cement matrix
水泥基
1.
The results indicate that reactive ingredient of the paint penetrated into the internal part of concrete reacts with cement matrix to produce insoluble needle-like crystal.
利用扫描电子显微镜、X射线衍射对水泥基渗透结晶型防水涂料涂层基体进行微观分析,研究涂料的活性组分渗透进入混凝土内发生的化学反应、反应可能生成的晶体产物及活性离子的渗透深度。
2.
In the experiment,carbon fibers were added into cement matrix,resulting not only in improved mechanical properties of cement,i.
试验中,将碳纤维加入到水泥基体中,不仅可改善水泥自身力学性能的缺陷,使其具有高强度、高模量、高韧性,更重要的是把普通的水泥建筑材料变成了具有自感知内部温度、应力和损伤及一系列电磁屏蔽性能的功能材料。
3.
Using casting powder or P-slag, at the standpoint of green and environmental materials and composites of cement matrix, this thesis has researched the subject of "non-autoclave and compound-foamed cement wall-block with light weight".
随着国家对环境问题的重视,铸造粉尘、磷渣等这类固体废弃物处理及资源化问题的日益突出,按照墙体材料改革的要求,从绿色环境材料和水泥基复合材料的观点出发,本课题研究了以铸造粉尘或磷渣为填充料的“轻质免蒸免烧水泥基复合发泡材料及制品”。
3) cement based
水泥基
1.
Effect of shrinkage reducing agent on shrinkage of cement based materials;
减缩剂对水泥基材料减缩效果的研究
2.
On the application of cement based capillary crystalline waterproof material
水泥基渗透结晶型防水材料的应用
3.
Rubberized asphalt emulsion modified cement concrete (ERACC) is a kind of cement based pavement composite which is made of cement mortar as matrix, and rubberized asphalt emulsion coated coarse aggregates as dispersed phase.
乳化橡胶沥青水泥混凝土（ＥＲＡＣＣ）是以水泥砂浆为连续相，以裹覆乳化橡胶沥青的粗集料为分散相的水泥基复合路面材料。
4) cementitious
[英][,si:mən'tiʃəs] [美][,simən'tɪʃəs]
水泥基
1.
Research of cementitious capillary crystalline waterproofing material modified by multi-component
多组分改性水泥基渗透结晶型防水材料的研究
2.
Analyses showed that early stage hydration of cementitious material mixed with KERIN waterproof materia.
利用空气渗透性能研制了科锐晶水泥渗透结晶型防水材料,并对其渗透结晶的作用机理分别对掺加防水材料的水泥浆体的电阻率、活性物质对水泥浆体材料的XRD形态影响,以及水泥基渗透结晶型防水材料对混凝土浆体不同渗透深度下的结晶形态进行了研究。
3.
Crack repair with cementitious capillary crystalline waterproofing (CCCW) material is a long process of penetration, settlement and crystallization.
水泥基渗透结晶型防水材料(CCCW)修复裂缝作用是一个渗透-沉淀-结晶的漫长过程。
5) cement base
水泥基
1.
Study on new type cement base anchoring material;
新型水泥基锚固材料研究
2.
It ascertained damage and destruction in the fiber cement based compound materials by testing variance of electric resistance at peak value.
利用电阻测试方法对碳纤维水泥基材料在循环共荷载下的内部损伤进行了监测研究,在循环荷载作用下,通过测试电阻峰值的变化,探知碳纤维水泥基复合材料内部的损伤和破坏,实现了碳纤维水泥基复合材料的自预警。
6) reference cement
基准水泥
1.
Influence of selection of reference cement on the blast-furnace slag activity index;
基准水泥的选择对矿渣粉活性检测的影响
2.
This article try converte common portland cement and concrete admixtures compatibility index to reference cement's,applying fuzzy math method,comparing with reference cement,making an judgement to the compatibility of them.
把普通硅酸盐水泥与外加剂相容性指标换算到基准水泥中来,应用模糊数学方法,与基准水泥进行比较,对普通硅酸盐水泥与外加剂的相容性作出评判。
补充资料：水泥基复合材料
分子式：
CAS号：
性质：以硅酸盐水泥为基体，以耐碱玻璃纤维、通用合成纤维、各种陶瓷纤维、碳和芳纶等高性能纤维、金属丝以及天然植物和矿物纤维为增强体，加入填料、化学助剂和水经复合工艺构成的复合材料。它比一般混凝土性能有所提高。以短切的耐碱玻璃纤维约3％～10％含量的复合材料为例，其密度为1600～2500kg/m3，抗冲强度8.0～24.5N·mm/mm2，压缩强度48～83MPa，热膨胀系数为(11～16)×10-6K-1。性能随所用原材料、配比、工艺和养护条件而异。水泥基复合材料基本上用于制造建筑构件，如内、外墙板、天花板等。
CAS号：
性质：以硅酸盐水泥为基体，以耐碱玻璃纤维、通用合成纤维、各种陶瓷纤维、碳和芳纶等高性能纤维、金属丝以及天然植物和矿物纤维为增强体，加入填料、化学助剂和水经复合工艺构成的复合材料。它比一般混凝土性能有所提高。以短切的耐碱玻璃纤维约3％～10％含量的复合材料为例，其密度为1600～2500kg/m3，抗冲强度8.0～24.5N·mm/mm2，压缩强度48～83MPa，热膨胀系数为(11～16)×10-6K-1。性能随所用原材料、配比、工艺和养护条件而异。水泥基复合材料基本上用于制造建筑构件，如内、外墙板、天花板等。