1) V-concentrating phase
钒富集相
1.
The enrichment of vanadium and crystallization and growth of V-concentrating phase in V-bearing steelmaking slag are studied by adding SiO_2 and Al_2O_3 with the method of melting-cooling.
采用熔融-冷却方法并在渣中分别添加SiO2和Al2O3进行改性,讨论了含钒钢渣中钒的富集以及钒富集相的结晶与生长。
2) vanadium concentration
钒富集
1.
Vanadium rich phases and vanadium concentration of vanadium bearing steel slag by addition of SiO_2;
含钒钢渣添加SiO_2后的钒富集相与钒富集行为
3) vanadium rich phase
富钒相
1.
Despite of the composition difference,slags from both factories showed similar mineral constitution after heat treatment,and no vanadium rich phase found inside.
为含钒钢渣设计富钒相,使钢渣中的钒主要富集于所设计的富钒相中。
4) vanadium enrichment characteristics
钒富集特征
5) Cu enriched phase
铜富集相
6) Enrichment of Si phase
硅相富集
补充资料：钒磷铁矿提钒
钒磷铁矿提钒
extraction of vanadium from the bear vanadium phosphosiderite
和94％。fantintiekuang tifan钒磷铁矿提钒(extraetion of vanadium frombear vanadium phosphosiderite)以含钒磷铁矿为原料制取五氧化二钒的帆提取方法。主要包括钠化焙烧和湿法漫出两道作业。直接用作提饥原料的是含饥磷铁。 含钒磷铁是饥磷铁矿电炉生产单质磷和磷肥的副产品。钒磷铁矿分布在美国爱达荷、蒙大拿、怀俄明、犹他等州，含Pz05 24%~32%、V:O。0.267%~0.625%和少量的铬、镍和钥等。美国克尔麦吉(Kerr-MeGee)化学公司所用的含钒磷铁含饥3.26%~5 .2%、磷24.7%~26.6%、铁59.9%一68.5%、铬3.4%一5.7%、镍。.84%~1%。先将含钒磷铁磨至粒度小于。.42mm，配入1.4倍纯碱和。.1倍的食盐在回转窑中于1043~lo63K温度下焙烧，钒便转变成水溶性的钠盐。熔烧块在加热到沸腾的水中浸出，钒、铬、磷均溶入浸出液。浸出浆液经过滤处理。滤液冷却结晶析出磷酸钠晶体，用离心机分离。晶体中如仍含有钒和铬，可用水重溶后再结晶分离，直到获得合格的磷酸钠(NaaPO;)晶体产品。若Na3PO‘结晶母液含磷高于0. 989/L时则要加入CaclZ，使其生成磷酸钙沉淀，然后水解回收钒。随后往母液中加入硝酸铅，沉淀出铬酸铅。此工艺的钒、铬和磷的回收率分别为85%、65%