1) argon shield
氩气保护
1.
A self-made vacuum melting and argon shield continuous unidirectional solidification equipment was used to produce copper tube with continuous columnar structure.
采用自行研制的真空熔炼、氩气保护连续定向凝固设备制备出具有连续柱状晶组织的铜管铸坯,分析了铜管铸坯生产中熔体温度、连铸速度、冷却水量,结晶器等对其的影响。
2.
Continuous unidirectional solidification equipment under conditions of vacuum melting and argon shield is designed and made on the basis of original traditional continuous unidirectional solidification equipment and vacuum system.
真空熔化氩气保护连续定向凝固设备,是在原有的常规连续定向凝固设备的基础上,加上真空系统而设计制造出来的。
3) argon shrouding
氩气保护罩
1.
Through investigating the oxidation behavior of metallic particles during atmosphericplasma spray process and their effect on coating microstructure with iron particles andNiCoCrAlY particles, a argon shrouding was developed which can decrease theoxidation of particles during atmospheric plasma spray process.
进而研制了能减少大气等离子喷涂过程中粒子氧化的氩气保护罩。
5) sintering in argon atmosphere
氩气保护烧结
1.
Porous TiNi alloy was prepared from element powder by sintering in argon atmosphere.
采用氩气保护烧结制备了多孔TiNi合金 ,并用图像分析的方法对其孔隙和孔隙率进行了研究。
6) Ar-shielding brazing
氩气保护钎焊
补充资料：氩39-氩40法测年
分子式：
CAS号：
性质：将含钾样品放入核反应堆中接受快中子照射，40K核被打进一个中子，而后放出一个质子，形成39Ar，用质谱计测定被照射样品的40Ar/39Ar比值，代替常规钾-氩法中40Ar/40K比值，从而计算出样品年龄的方法，计算公式如下：t=λ-1ln(1+J•40Ar/39Ar)。式中J=39Ar/40Ar•λ/λkΔT∫φ(ε)σ(ε)dε是样品照射持续的时间，Ф(ε)是能量为ε时的中子通量，σ(ε)为39K(n，p)39Ar的反应截面，实验中用一已知年龄(ts)的标准与待测样品一块进行辐照，由下式求得J值：J=(eλt-1)/(40Ar/39Ar)。此方法解决了过去钾、氩分别由不同方法测定所产生的不同误差使年龄精度较低的弊端；同时由于照射后样品氩的释放可采用阶段加温方法，对一个样品便可获得一系列的表面年龄，最终得到代表矿物或岩石结晶的稳定坪年龄；或由等时线法处理得到样品的年龄、认识外来氩的混入状况。
CAS号：
性质：将含钾样品放入核反应堆中接受快中子照射，40K核被打进一个中子，而后放出一个质子，形成39Ar，用质谱计测定被照射样品的40Ar/39Ar比值，代替常规钾-氩法中40Ar/40K比值，从而计算出样品年龄的方法，计算公式如下：t=λ-1ln(1+J•40Ar/39Ar)。式中J=39Ar/40Ar•λ/λkΔT∫φ(ε)σ(ε)dε是样品照射持续的时间，Ф(ε)是能量为ε时的中子通量，σ(ε)为39K(n，p)39Ar的反应截面，实验中用一已知年龄(ts)的标准与待测样品一块进行辐照，由下式求得J值：J=(eλt-1)/(40Ar/39Ar)。此方法解决了过去钾、氩分别由不同方法测定所产生的不同误差使年龄精度较低的弊端；同时由于照射后样品氩的释放可采用阶段加温方法，对一个样品便可获得一系列的表面年龄，最终得到代表矿物或岩石结晶的稳定坪年龄；或由等时线法处理得到样品的年龄、认识外来氩的混入状况。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条