1) template
[英]['templeɪt] [美]['tɛm'plet]
模板剂
1.
Pore diameter adjustment of mesoporous alumina with different templates;
不同模板剂对介孔氧化铝孔径调节作用
2.
Research and Application of Template During Synthesis of Mesoporous Molecular Sieves;
介孔分子筛合成中模板剂的研究与应用
3.
The effect of template on SAPO-11 molecular sieves synthesis;
SAPO-11分子筛合成中模板剂的作用
2) template agent
模板剂
1.
CuMCM-41 mesoporous molecular sieves were synthesized by the hydrothermal method and using inorganic salt sodium silicate and copper chloride as raw materials,and cetyl trimethyl ammonium bromide as template agent.
6H2O)等无机盐为原料,十六烷基三甲基溴化铵为模板剂,通过水热法合成CuMCM-41介孔分子筛。
2.
Using cetyl trimethyl ammonium bromide as the template agent,the mesopouous silica was synthesized under different alkaline conditions.
以十六烷基三甲基溴化铵作为模板剂,在不同碱性条件下合成介孔二氧化硅材料,并对它的合成方法、合成因素的影响等方面进行阐述。
3.
Mesoporous titania was synthesized by solvent-thermal method,using sodium dodecyl sulphonate as template agent,using titanium tetrachloride as raw material and using butanol and octanol as solvent,respectively.
以四氯化钛为原料,采用十二烷基磺酸钠为模板剂,分别以丁醇和辛醇为溶剂,通过溶剂热法合成介孔二氧化钛。
3) templates
模板剂
1.
Characterization and Thermal Decomposition Modes of SAPO-34 Molecular Sieves Synthesized with Different Templates;
不同模板剂合成SAPO-34分子筛的表征与热分解过程研究
2.
Mesoporous zirconia was prepared by a convenient process with cetyltrimethylammonium bromide(CTAB) as templates,and zirconyl chloride octahydrate(ZrOCl_2·8H_2O) as zirconium resource.
8H2O)为锆源,十六烷基三甲基溴化铵(CTAB)为模板剂,制备了介孔氧化锆。
3.
Generally speaking, the synthetic course has closed relations with the choice of reactive materials, templates, synthesis temperature, pH, molar density ratio of surf and SiO2.
介绍了M41S中孔分子筛材料的合成过程以及表面活性剂模板法合成中孔分子筛的影响因素,总的来说,它的合成与反应原料、模板剂、合成温度、酸碱度、模板剂与SO2前体摩尔浓度之比的选择有密切关系。
4) templating agent
模板剂
1.
It is found that using a cationic surfactant ( CTAB ) as templating agent with ammonia as precipitator after drying and calcination results in high surface area mesostructured Ce.
以3种表面活性剂(阳离子型表面活性剂CTAB,阴离子表面活性剂十二烷基硫酸钠和非离子嵌段型表面活性剂P123)为模板剂, Ce(NO3)3作为前驱体,制备了CeO2。
5) co-templates
双模板剂
1.
Synthesis and characterization of zeolite ZSM-11 with co-templates in hydrothermal system;
纯相ZSM-11分子筛在双模板剂水热体系中的合成及表征研究(英文)
6) amine template
胺模板剂
1.
Synthesis of ZnS hollow nanospheres with different amine templates;
不同胺模板剂合成有孔硫化锌纳米空球
补充资料：8105涂料印花黏合剂、HF自交型涂料印花黏合剂、印染黏合剂DE、SC-183涂料印花黏合剂、黏合剂7601
分子式：
CAS号：
性质：又称8105涂料印花黏合剂、HF自交型涂料印花黏合剂、印染黏合剂DE、SC-183涂料印花黏合剂、黏合剂7601或7601自交型黏合剂T/C。外观为带蓝色荧光的白色乳液。pH值5～6。含固量38%～40%。主要成分是丙烯酸丁酯、丙烯腈和N-羟甲基丙烯酰胺的共聚物。适用于棉及涤/棉混纺织物的涂料印花，高温熔烘(180℃下，15min)不泛黄。
CAS号：
性质：又称8105涂料印花黏合剂、HF自交型涂料印花黏合剂、印染黏合剂DE、SC-183涂料印花黏合剂、黏合剂7601或7601自交型黏合剂T/C。外观为带蓝色荧光的白色乳液。pH值5～6。含固量38%～40%。主要成分是丙烯酸丁酯、丙烯腈和N-羟甲基丙烯酰胺的共聚物。适用于棉及涤/棉混纺织物的涂料印花，高温熔烘(180℃下，15min)不泛黄。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条