1) molybdenum carbide
碳化钼
1.
An investigation on the hydrodenitrogenation performance of molybdenum carbide catalyst;
碳化钼催化剂加氢脱氮性能研究
2.
Study on n-heptane isomerization on β zeolite supported molybdenum carbide catalyst;
正庚烷在β沸石负载碳化钼催化剂上的异构化研究
3.
Preparation of molybdenum carbide catalyst and its hydrodesulfurization performance for thiophene;
碳化钼催化剂的制备及噻吩加氢脱硫性能
2) molybdenum(tungsten)carbide
碳化钼(钨)
3) molybdenum carbide
碳化钼<冶>
4) molybdenum carbonitride
碳氮化钼
1.
The as-prepared product was characterized by x-ray diffraction(XRD),x-ray photoelectron spectroscopy(XPS),low-temperature nitrogen adsorption and elemental analyzer,and confirmed that it was a mixture of molybdenum carbide(β-Mo2C) and molybdenum carbonitride(Mo2CxNy).
采用X射线衍射(XRD)、X射线光电子能谱(XPS)、低温氮吸附、元素分析等方法对催化剂进行了表征,发现碳氮夹杂钼基催化剂实为碳化钼(β-Mo2C)与碳氮化钼(Mo2CxNy)的混合物。
补充资料：碳化钼陶瓷
分子式：
CAS号：
性质：钼与碳的化合物为主要成分的陶瓷。主要有两类。(1)以碳化二钼(Mo2C)为主晶相的陶瓷。呈暗灰色。理论密度9.2g/cm3。熔点2690℃。莫氏硬度7。显微硬度1800kg/mm3(负荷50g)。弹性模量22100kg/mm2。热导率6.7×106W/(m·K)。2300℃以上分解。(2)以一碳化一钼(MoC)为主晶相的陶瓷。理论密度8.88g/cm3。熔点2700℃。一般先制成碳化钼粉末(采用钼与碳直接化合法、金属氧化物与碳的还原一化合法、气相沉积法和自蔓延高温合成法)，然后在真空或还原气氛下在碳管炉、钼丝炉、高频真空炉中进行烧结(多采用反应烧结、热压烧结和热等静压烧结)而制成。主要用作超硬工具材料、耐磨材料、发热体材料以及高温结构材料。
CAS号：
性质：钼与碳的化合物为主要成分的陶瓷。主要有两类。(1)以碳化二钼(Mo2C)为主晶相的陶瓷。呈暗灰色。理论密度9.2g/cm3。熔点2690℃。莫氏硬度7。显微硬度1800kg/mm3(负荷50g)。弹性模量22100kg/mm2。热导率6.7×106W/(m·K)。2300℃以上分解。(2)以一碳化一钼(MoC)为主晶相的陶瓷。理论密度8.88g/cm3。熔点2700℃。一般先制成碳化钼粉末(采用钼与碳直接化合法、金属氧化物与碳的还原一化合法、气相沉积法和自蔓延高温合成法)，然后在真空或还原气氛下在碳管炉、钼丝炉、高频真空炉中进行烧结(多采用反应烧结、热压烧结和热等静压烧结)而制成。主要用作超硬工具材料、耐磨材料、发热体材料以及高温结构材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条