1) DC magnetic field
直流磁场
1.
It is found that the primary Si becomes longer and longer and the eutectic structure becomes more and more dense with the decrease of the temperature at which the DC magnetic field is applied to the sample.
结果表明:随着施加直流磁场温度的降低,初生Si变得越来越长,共晶组织也变得越来越细密;随着施加交流磁场温度的降低,初生Si变得越来越粗大,共晶组织无明显变化。
2.
The influence of ageing temperature of the negative AE effect and internal friction Q-1 of dispersion-hardened Elinvar alloy Fe-Ni-Cr-Ti under the action of a DC magnetic field was studied.
研究了时效温度对直流磁场作用下Fe-Ni-Cr-Ti弥散硬化埃林瓦合金负△E效应和内耗Q~(-1)影响。
3.
The effects of DC magnetic field on friction and wear of ferromagnetic materials at different loads have been studied.
对直流磁场影响下铁磁性材料载荷变化时摩擦磨损的研究表明,各种载荷下磁场都能显著减小摩擦、减轻磨损。
2) direct current magnetic field
直流磁场
1.
The friction and wear characteristics of 45 steel pan against 45 steel pin under direct current magnetic field and at dry sliding friction and room temperature were studied.
在室温下,将45#钢盘-销摩擦副置于直流线圈产生的磁场中,研究直流磁场对45#钢干滑动摩擦磨损性能的影响。
2.
08mT in direct current magnetic field and reaches the maximum at 0.
结果表明：随着直流和交流磁场强度的增加,合金的阻尼性能都呈现先增加后下降的变化规律,但直流磁场时合金在0。
3.
For this issue, the method, which is the quality controlling of spot welding in the external direct current magnetic field, will be discussed by this article.
针对这个问题,本文探讨了外加直流磁场改善点焊质量的方法。
3) direct magnetic field
直流磁场
1.
Effection on microstructure of AZ91D magnesium alloy by direct magnetic field under different temperature;
不同通磁温度下直流磁场对AZ91D镁合金凝固组织的影响
2.
The effects of the direct magnetic field treatment on the microstructure and electrochemical performances of hydrogen storage alloys during their solidification process were studied.
研究了贮氢合金凝固过程中施加直流磁场处理对其组织结构和电化学性能的影响。
3.
Eutectic Al Si composite in situ was fabricated under the condition of direct magnetic field.
在直流磁场作用下制备了 Al- Si共晶自生复合材料 ,其组织发生共晶分离 ,在试棒外表层形成硅的富集层 ,其厚度随磁感应强度的增大而增加。
4) Stationary Magnetic Field
直流磁场
1.
Effects of Stationary Magnetic Field on Microstructure of 7075 Aluminum Alloy;
直流磁场对7075铝合金组织结构的影响
2.
3%Cu alloy solidified under a stationary magnetic field was measured through a way of double electric bridges,the liquidus and solidus temperature of the alloy under the stationary magnetic field were determined by the analysis of the curve when the intensity of the magnetic field was 0.
3%Cu合金在直流磁场下凝固的电阻-温度曲线,通过对曲线的分析,确定了合金在磁场强度为0。
5) steady directcurrent magnet
稳恒直流磁场
6) cocurrent pulsating magnetic field
直流脉动磁场
补充资料：磁放大器直流调速
磁放大器直流调速
speed control of DC mo-tor by magnetic amplifier
负载串联，然后通过桥式整流接到交流电压U.。 控制信号U。为。时，交流绕组加上交流电源后，两个铁芯均接近饱和但未饱和，电源电压全部降在交流绕组上，Ud输出接近为。。 当电压为正半周时，控制绕组上加有如图极性的控制信号U。，则铁芯2磁通将减少，铁芯1磁通将增加，并将出现饱和。一旦饱和，则Lol及Lal均无感应电动势而相当于一根导线，再加上控制电源内阻很小，Lol就相当于把LcZ短路。短路绕组的存在迫使铁芯2里的磁通不能变化，因而交流绕组LaZ两端的感应电动势亦为0.由于Lal、LaZ两个交流绕组的感应电动势均为。，所以电源电压U.从饱和瞬时开始将被输出到与交流绕组串联的直流电动机电枢两端。当交流电源工作于负半周时，则LaZ先达到饱和，强迫Lal中的磁通不变，翰出负电压，通过二极管整流桥把翰出的电压整流成单方向的脉动电压Ud。┌───┐│! ││卜肠盈││广 │└───┘ ┌──┐┌───┐│凡 ││! ││〕忆││巨肠盈││三 ││广 ││ │└───┘│ │ └──┘泣 磁放大界供电进行直流调速的原理图 若控制信号加大，那么铁芯中磁通达到饱和的时间提前，翰出电压就相应加大.将整流后的电压供给直流电动机电枢或励磁绕组时，直流电动机的转速就得到控制。其调速范围一般为1，l。，在有速度反债时可达到1:100. 磁放大器按照铁芯结构的不同类型可分为O型、n型和111型，按容t来分，10 kw以下一般用单相线路，大容t的要用三相线路，容量可达800 kw，在要求可逆时则需采用两相线路。 由于磁放大器铁芯是由硅钢片构成，无旋转部分，控制绕组与主回路互相绝缘，且可以设计成多个控制绕组进行复合控制，所以结实可靠，过载能力强，噪声小，控制绕组之间没有电的联系，控制灵活，因而适合于各种需要改变电压的自动控制场合。 20世纪60年代左右出现了晶体管，它不像磁放大器那样有铁芯和绕组，相比之下具有体积小、材料省、重t轻、效率高、放大倍数大的优点，所以磁放大器直流调速已被晶体管相位控制直流调速所取代(见晶闸借相位拉制立流调速)。C .fangdoq一Zhillu tloosu磁放大器直流调速(speed eontrol ofL〔motor by magnetie amplifier)利用磁放大器输出电压可调的直流电，实现直流电动机调速的技术。 磁放大器的工作原理和进行直流调速的原理图如图所示。图中虚线框为磁放大器，它有两个铁芯1和2.每个铁芯上装有两个绕组，一个称控制绕组L。，一个称交流绕组La，两个控制绕组反极性串联后接到低内阻直流控制电压队，两个交流绕组顺极性相连后与